In the present work, FeMn13-40 wt.% TiC composite was fabricated by Pulsed Electric Current Sintering (PECS) process at different temperatures between 990 and 1020<sup>o</sup>C under a pressure of 60 MPa with a holding time of 5 min in the vacuum. Phases identification was done using the X-ray diffraction. The relative density, microstructure and hardness of the samples were characterized. The results showed that the relative density of FeMn13-TiC composite increased with the increase of sintering temperature. The highest relative density (96.19%) and the hardness (70.54 HRC) of the sample were achieved by PECS process, namely sintering at the temperature of 1020<sup>o</sup>C under the applied pressure of 60 MPa for 5 min.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.