Magnetic MCM-41 of large surface area (ca. 800 m2 g−1) and high magnetization (ca. 8.3 emu g−1) was prepared at a reasonable iron oxide nanoparticles loading of 10 wt % by a two-step synthesis process. The 8 nm iron oxide nanoparticles (i.e., 30 m2 g−1) were embedded in the MCM-41 with no observable effects on the particle morphology and pore symmetry, but a slight change (i.e., <20%) in the textural properties and surface chemistry was detected. Aminopropyls (2.7 mmol g−1) were grafted on the mesopore channels followed by the adsorption of 1.2 mmol g−1 Fe3+ to prepare selective adsorbents for arsenic(V) and chromium(VI) oxyanions. Detailed analyses indicated that the surface modifications of the magnetic and nonmagnetic MCM-41 by aminopropyls and Fe3+ yield similar site chemistry and accessibility. The Fe3+-magMCM-41 and Fe3+-MCM-41 displayed comparable adsorption capacity and selectivity. Both adsorbed only As(V) and Cr(VI) oxyanions (i.e., 1.0 and 2.0 mmol g−1, respectively), and none of the Cu(II). The magnetic adsorbent was easily dispersed in aqueous solution and can be removed by a magnet (1550 G) at a rate of 1 cm min−1 compared to 0.004 cm min−1 by gravity.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.