Maraging steel is an alloy of Ni-Fe having very low carbon content. These steel is having superior properties like toughness and strength without losing its malleability. In the present work 5mm thick Maraging steel plates were welded using GTAW process with maraging steel filler wire. This paper attempts to analyse the microstructure and mechanical properties of the weldment. Post weld heat treatment (PWHT) was carried out at 480°C. Strength of welded joint of as-weld and PWHT was tested using ultimate tensile machine (UTM). Both the tensile specimen (As-weld and PWHT) breaks at base metal zone. The quality of joint at micro-level was analysed using optical microscopy. PWHT sample have finer grain compare to weld sample. Different phases transformation was observed in microstructures. Microhardness was also observed at different location in and around the joint. It was also observed that the fusion zone and heat affect zone (HAZ) of PWHT has higher value of Microhardness compare to weld sample.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.