Objectives:To evaluate the influence of various photoactivation techniques on the internal gap, Knoop-hardness, and polymerization depth of silorane- and methacrylate-based composites in Class II restorations.Methods:Preparations were made in third molars (n = 10), according to composites (Filtek P60: methacrylate; Filtek P90: silorane) and photoactivation techniques (OC: occlusal photoactivation (control); OBL: occlusal+buccal+lingual photoactivation; and BLO: buccal+lingual+occlusal photoactivation (transdental)). Composites were inserted in two increments, both individually photoactivated for 20s. After 24h, specimens were sectioned and the ratio of internal gaps to interface length (%) recorded. Hardness was tested across the transversal section of restorations (1–4 mm below the surface).Results:Silorane restorations showed significantly lower gaps compared with methacrylate, regardless of polymerization technique (P<.05). Supplementary energy dose in OBL and BLO protocols caused significant increase in gaps in silorane restorations (P<.05). For methacrylate restorations, OBL activation caused significantly higher gap formation (P<.05). Significantly lower hardness values were seen for silorane than for methacrylate composites (P<.05), regardless of depth and photoactivation. Significantly higher hardness values were seen in BLO activation for methacrylate restorations compared with control (P<.05); for silorane, no differences were observed. Significantly higher hardness values were observed at 1 and 3 mm compared to 2 and 4 mm for both composites.Conclusions:Internal gaps and hardness are affected by composite type and photoactivation. Despite the reduced values, hardness of silorane is not influenced by photoactivation or by depth. Internal gaps are dependent on the energy dose for both composites, with silorane showing lower internal gaps.
This study compared the hydrolytic degradation of composite restorations based on methacrylate and silorane systems regarding bond strength and marginal adaptation. Materials and methods. Sixty bovine incisors were ground flat to obtain a 2-mm thick slice in which conical preparations were made. The specimens were randomly distributed into four groups (n = 15) according to the restorative system (silorane-Filtek LS/P90 adhesive; methacrylate-Filtek P60/Adper Easy Bond) and the degradation protocol (control: immediate evaluation; hydrolytic degradation: 6 months storage in water at 37°C). Marginal adaptation was evaluated using a dye staining technique. Digital images of the stained gaps were obtained to calculate the marginal gap (%), the ratio between the stained margins and the total length of the margin. Push-out bond strength test was conducted (0.5 mm/min). Marginal adaptation data was submitted to Kruskal-Wallis test and the bond strength data to two-way ANOVA/Tukey's test (α = 0.05). Results. The marginal adaptation was neither affected by the restorative system nor by the degradation protocol, although the number of perfect sealed reduced after 6 months. No significance was observed among the groups. No significance was noted between the silorane- and the methacrylate-based restorations for immediate bond strength. After the hydrolytic degradation, the silorane system showed higher bond strength then the methacrylate restorations. Conclusion. The silorane and methacrylate restorative systems produce restorations with similar immediate interfacial quality and 6 months of water storage does not cause significant bonding degradation for both systems. The silorane restorations show an increase in the bond strength after 6 months.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.