The present work focusses on improving the mechanical and tribological properties of Al-5Si-3Cu alloy and Ni-coated TiC reinforced composite fabricated through liquid metallurgy route, through T6 heat treatment. Good interfacial bonding was developed between the matrix and coated reinforcement on microstructural investigation. There was an improvement in hardness for heat-treated alloy and composite by 34.5% and 14.7% respectively. Tensile strength for heat-treated alloy and composite was enhanced by 25.9% and 30.6% respectively. Pin on disc dry sliding wear test was carried out for Ni-coated TiC heat-treated composite for varying loads (10, 20, 30N), distances (500, 1000, 1500m) and velocities (1, 2, 3m/s) by using Taguchi's L27 Orthogonal Array. It was concluded that load had the highest influence on wear rate (71.88%), whereas the effects of sliding distance (8.23%) and velocity (3.45%) were nominal. Wear analysis revealed that, wear rate increased with an increase in load and sliding velocity and decreased with increasing sliding distance. Defects like delamination, grooving, and protrusions were observed on the worn surface. Thus, this kind of Nicoated TiC reinforced composites can be used in camshafts, bearings and bushes for better wear resistance.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.