The stringent demand to develop lightweight materials with enhanced properties suitable for various engineering applications is the focus of this research work. Industrial wastes such as fly ash (FA) and S-glass-fibres (GF) were used as reinforcement materials for high-strength alloy, i.e., Al 7005. Stir casting routes were employed for fabricating the four samples, Al 7005, Al 7005 + 5% GF, Al 7005 + 6% FA and Al 7005 + 5% GF + 6% FA. The extrusion process with different extrusion ratios (ER: 5.32:1, and 2.66:1) was used to examine the properties of all four samples. Extruded samples with ER: 5.32: 1 resulted in equiaxed grains with refined structure compared to stir casting parts. The effect of the extrusion process and the addition of reinforcements (GF and FA) on the gravimetric, electrochemical, and electrochemical impedance corrosion behaviour of Al 7005 composites in 1M HCl (Hydrochloric acid) solution were investigated. The results of all three corrosion methods showed that Al 7005 + 6% FA exhibited higher corrosion resistance. Corrosion rate of Al 7005, Al 7005 + 5% GF, Al 7005 + 6% FA and Al 7005 + 5% GF + 6% FA is found equal to 3.25, 2.41, 0.34, and 0.76 mpy, respectively. The FA particles remain inert and act as a physical barrier with corrosive media during the corrosion test. GF undergoes fibre degradation or disrupts the continuity of the glass network as a result of fibre leaching, which increases the corrosion rate in the sample. The gravimetric study showed that the corrosion rates decreased with an increase in extrusion ratio, which might be due to corrosion passivation increases and improved properties. The scanning electron microscopy reveals that corrosion fits, flakes and micro-cracks were observed more in the as-cast composites than that of extrusion composites, promoting the corrosion rate.
The effect of extrusion ratio and addition of glass and fly ash on microstructural, mechanical properties, and fracture behavior of Al composites is examined. Both the composites and hybrid composites are prepared by the liquid metallurgical technique. Microstructure, extrusion effect on hardness, tensile properties, and fracture are studied using an optical micrograph, hardness tester, Universal Testing Machine, and scanning electron microscope, respectively. Experimental results show that increasing the extrusion ratio leads to a significant enhancement in mechanical properties such as tensile, compression, and yield strength and Young’s modulus, but results in a small reduction of ductility. It has been revealed that the presence of glass and fly ash improve the mechanical properties significantly with a slight reduction in ductility compared to the Al alloy. Fracture behaviour of the base alloy and composites show intergranular ductile and brittle cleavage mode failure as observed by SEM.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.