Copper–tungsten composite materials are developed for applications such as electrical contacts, resistance electrodes, and contact tips in welding guns as well as for components requiring higher wear resistance. In addition to the aspect of improved performance, it is scientifically interesting to assess the tribological properties, and therefore the objectives of the present work include, to determine the role of W additions in improving the fretting wear resistance of Cu for electrical applications, to determine the optimum concentration for W additions, and to identify the mechanisms responsible for fretting wear improvements. In addressing these issues, a planned set of fretting wear tests were conducted on powder metallurgically processed Cu–W composites (maximum W content of 20 wt %) against steel counterbody under varying load (up to 10 N) for 10,000 cycles. It has been observed that at lower loads of 2 N, the coefficient of friction (COF) recorded was ∼0.9 for the Cu–20 wt % W/steel, whereas it was ∼0.85 for a pure Cu/steel couple. Under similar operating conditions with the increase in load, the COF decreases to 0.5 at 10 N load, irrespective of the composition of the Cu–W composite. Furthermore, the incorporation of 5 wt % W has reduced the volumetric wear loss by 4–6 folds in comparison to unreinforced Cu. The addition of even higher percentage of W has led to increase its wear resistance by ∼10 folds. Under the investigated conditions, the wear rate systematically decreases with the increase in load for all the tested Cu–W composites. Based on the topographical observation of worn surfaces, it is observed that wear mechanisms for the Cu and Cu–W composites are tribochemical wear, adhesive wear, and abrasive wear. The incorporation of harder W particles (5 wt % or more) help in abrading the steel ball and in forming a dense tribolayer of FexOy, which effectively reduces wear rate and hence, increases wear resistance of the Cu–W composite surface in reference to unreinforced Cu.
This book presents the abstracts of the papers presented to the Online National Conference on Research and Developments in Material Processing, Modelling and Characterization 2020 (RDMPMC-2020) held on 26th and 27th August 2020 organized by the Department of Metallurgical and Materials Science in Association with the Department of Production and Industrial Engineering, National Institute of Technology Jamshedpur, Jharkhand, India.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations –citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.