Porous V2O5/TiO2 nanoheterostructure films with different atomic ratios of Ti/V (4:1, 2:1, 1:1, and 1:2) were synthesized by a sparking method for the first time. The sparking method, which is a simple and cost-effective process, can synthesize highly porous and composite films in one step. Field-emission scanning electron microscope (FE-SEM) images revealed the porosity morphology of all prepared samples. V2O5/TiO2 nanoheterostructure films were confirmed by Raman spectroscopy, high-resolution transmission electron microscopy (HRTEM), and X-ray photoelectron spectroscopy (XPS). The secondary particle size and band gap of the samples were highly correlated to the V2O5 proportion, resulting in enhanced visible-light absorbance. V2O5/TiO2 nanoheterostructure films at an atomic ratio of 1:1 showed the highest photocatalytic performance, which improved the degradation rate up to 24% compared to pure TiO2 film. It is believed that the formed nanoheterostructure and greater portion of V4+ ions are reflected by this ratio.
Stretchable and compressible strain sensors play an essential role in various fields with uses ranging from automotive components to medical devices. This study reports on the fabrication and characteristics of stretchable strain and pressure sensors constructed using a carbon nanotube and graphene composite. The sensors were used for gait analysis, an important step in the diagnosis and management of movement disorders. The stretchable and compressible strain sensors were used to measure peak knee sagittal angles and forces under the feet when walking. Gait analysis is usually performed within a laboratory. However, in this research we propose a shift to gait assessments conducted via long-term daily monitoring using wearable devices.
We have used an external electric field to increase both the uniformity and deposition rate of TiO2 films. The experiment is carried out by sparking-off titanium wires with a high dc voltage of 1 kV (field int = 10 kV/cm) and a limited current of 3 mA. The external electric fields ( ext) of 3, 6, and 9 kV/cm were applied to the sparking system for 1-5 hours. The as-deposited film morphology was characterized by scanning electron microscopy. The results clearly show that the films are only deposited on the external electric field area. Furthermore, the deposition rate of the films increased from 40.7% to 77.8% in the presence of the external electric field of 9 kV/cm. The effects of an external electric field on both the deposition rate and uniformity of films are investigated and described. K e y w o r d s: TiO2 film, sparking process, external electric fields.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.