The method of ultrasound irradiation is used for anchoring metallic nanocrystals (Ag, Au, Pd, and Pt) onto the surface of polystyrene spheres. In former studies, almost all the sonochemically prepared, coated metallic nanomaterials were formed as amorphous nanoparticles (Pol, V. G.; et al. Langmuir 2002, 18, 3352; Pol, V. G.; et al. Chem. Mater. 2003, 15, 1111; Zhong, Z. Y.; et al. Chem. Mater. 1999, 11 (9), 2350; Pol, V. G.; et al. Chem. Mater. 2003, 15, 1378), which were coated on various substrates (silica spheres, carbon spherules, titania, and alumina). On the other hand, the noble metal nanoparticles deposited on polystyrene spheres via ultrasound irradiation yielded nanocrystalline Ag, Au, Pd, and Pt particles on the surface of polystyrene as as-synthesized materials. The sonochemical mechanism is proposed based on chemical interactions between the particles.

A very simple, efficient, and economical synthetic technique, which produces fascinating fullerene-like Ni-C (graphitic) core-shell nanostructures at a relatively low temperature, is reported. The thermal dissociation of Ni acetylacetonate is carried out in a closed vessel cell (Swagelok) that was heated at 700 degrees C for 3 h. The encapsulation of ferromagnetic Ni nanospheres into the onion structured graphitic layers is obtained in a one-stage, single precursor reaction, without a catalyst, that possesses interesting magnetic properties. The magnetoresistance (MR) property of Ni nanospheres encapsulated in a fullerene-like carbon was measured, which shows large negative MR, of the order of 10%. The proposed mechanism for the formation of the Ni-C core-shell system is based on the segregation and the surface flux formed in the Ni and carbon particles during the reaction under autogenic pressure at elevated temperature.

The thermal decomposition of commercial silicone grease was carried out in a closed reactor (Swagelok) that was heated at 800 degrees C for 3 h, yielding a SiO2-carbon composite with a BET surface area of 369 m2/g. The bulk conductivity (5.72 x 10(-6) S x cm(-2)) of the SiO2-carbon composite was determined by impedance measurements. The as-prepared SiO2-carbon composite was further annealed at 500 degrees C in air for 2 h, which led to the formation of white paramagnetic silica particles (confirmed by ESR), possessing a surface area of 111 m2/g. The present synthetic technique requires unsophisticated equipment and a low-cost commercial precursor, and the reaction is carried out without a solvent, surfactant, or catalyst. The mechanism for the formation of a porous SiO2-carbon composite from the silicone grease is also presented.