In this study, we utilized electrospun silica fibers (ESFs) as reinforcement in sandwiched nylon-6 composites. The silica fibers were fabricated via electrospinning of sol-gel precursor, prepared from tetraethyl orthosilicate. The process yielded non-woven silica fiber mats with fiber diameter about 350 nm, which is much smaller than conventional glass fibers. Each ESF mat was sandwiched in between two nylon-6 sheets and the layers were compression-molded to produce a composite sample. These composites were prepared with varying silica fiber content, approximately at 0, 0.5, 1.0, and 1.9 wt%. The ESF blended well and chemically bonded with the nylon matrix, as observed through scanning electron microscopy and Fourier transform infrared spectroscopy. Tensile tests revealed that tensile modulus and tensile strength increased with ESF content. Notch Izod impact test showed that impact strength also increased with ESF content. The tensile and impact properties were significantly improved, considering the use of such low silica fiber percentages, which could be due to ultra-fine fiber diameter and fiber continuity. From flexural test, however, flexural modulus and flexural strength decreased slightly by the addition of ESF. Specimen geometry and fabrication process play important roles in governing the composites mechanical behavior. POLYM. COMPOS., 00:000-000,
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.