We have studied the electrical characteristics and optical properties of GaN/InGaN multiple quantum well (MQW) light-emitting diodes (LEDs) grown by metalorganic chemical vapor deposition. It appears that there is an essential link between material quality and the mechanism of current transport through the wide-bandgap p-n junction. Tunneling behavior dominates throughout all injection regimes in a device with a high density of defects in the space-charge region, which act as deep-level carrier traps. However, in a high-quality LED diode, temperature-dependent diffusion-recombination current has been identified with an ideality factor of 1.6 at moderate biases. Light output has been found to follow a power law, i.e., in both devices. In the high-quality LED, nonradiative recombination centers are saturated at current densities as low as 1.4 10 2 A/cm 2 . This low saturation level indicates that the defects in GaN, especially the high density of edge dislocations, are generally optically inactive.Index Terms-Carrier injection, GaN, light-emitting diode (LED), multiple quantum well.

Nickel-titanium alloy (Nitinol) is a metallic biomaterial that has a unique thermal shape memory, superelasticity, and high damping properties. Nitinol is potentially very useful in orthopedic surgery, for example. At present, there are not enough confirmative biocompatibility data available on Nitinol. The aim of our study was to clarify the primary cytotoxicity and corrosion rate of Nitinol in human cell cultures. Comparisons were made with stainless steel (Stst), titanium (Ti), composite material (C), and control cultures with no test discs. Human osteoblasts (OB) and fibroblasts (FB) were incubated for 10 days with test discs of equal size, 6 x 7 mm. The cultures were photographed and the cells counted. Samples from culture media were collected on days 2, 4, 6, and 8, and the analysis of metals in the media was done using flameless atomic absorption spectrophotometry. The proliferation of FB was 108% (Nitinol), 134% (Ti) (p < 0.02), 107% (Stst), and 48% (C)(p < 0.0001) compared to the control cultures. The proliferation of OB was 101% (Nitinol), 100% (Ti), 105% (Stst), and 54% (C) (p < 0.025) compared to the controls. Initially, Nitinol released more nickel (129-87 micrograms/L) into the cell culture media than Stst (7 micrograms/L), but after 2 days the concentrations were about equal (23-5 micrograms/L versus 11-1 micrograms/L). The titanium concentrations from both Nitinol and Ti samples were all < 20 micrograms/L. We conclude that Nitinol has good in vitro biocompatibility with human osteoblasts and fibroblasts. Despite the higher initial nickel dissolution, Nitinol induced no toxic effects, decrease in cell proliferation, or inhibition on the growth of cells in contact with the metal surface.

Articles you may be interested inHigh quality AlGaN solar-blind Schottky photodiodes fabricated on AIN/sapphire template Appl.

No abstract