This study evaluates the use of a barrel atmospheric plasma system for the treatment of acrylonitrile butadiene styrene and polylactic acid polymer particles. Treatments were carried out in a helium discharge with either oxygen or nitrogen addition. The plasma activated polymer particles were then used to prepare filaments, which in‐turn were then used to fabricated parts by additive manufacturing. The resultant dog bone polymer parts exhibited up to a 22% increase in tensile strength, compared to parts fabricated using unactivated polymer particles. The explanation for the increased mechanical strength is the enhanced activation of the treated polymer particles, as well as the removal of contaminations from the polymer surface.
The objective of this study is to investigate the use of an air atmospheric plasma jet for the treatment of sized basalt fibers, used in the fabrication of continuous fiber‐reinforced polypropylene filaments. The plasma treatments were carried out both at a laboratory scale, as well as in‐line during the production of fiber‐reinforced filaments. The latter was carried out at a fiber processing speeds of approximately 15 m/s, just immediately before the polymer coating of the fiber by extrusion. After the air plasma treatment, the water contact angle of the sized basalt fiber decreased from 86° to <10°. X‐ray photoelectron spectroscopy analysis demonstrated that the treatment yielded enhanced levels of oxygen functionality on the fiber surface. After coating with polypropylene, it was observed that there was consistently more homogeneous polymer layer deposited onto the plasma‐activated fiber, compared with that on the unactivated control fiber. The resulting polymer filament with embedded basalt fiber was used to fabricate mechanical test specimens by three‐dimensional printing (fused filament fabrication method). Both three‐point bending tests and short beam strength tests were performed. A comparison study was carried out between test specimens fabricated using sized basalt fiber, with and without the plasma pretreatment. The flexural modulus and maximum shear stress were found to increase by 12% and 13%, respectively, for composite's fabricated using the plasma pretreated basalt fibers. This increased mechanical strength is likely to be due to an increase in interfacial bond strength between the polymer and fiber, with an associated reduction in the level of air incorporation around the basalt filaments as demonstrated using computed tomography analysis.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.