SiC-based components are sometimes susceptible to aqueous dissolution in LWR coolant environments. To address this issue, ~10 μm thick Cr coatings was deposited on reaction-bonded silicon carbide (RBSC) plates by magnetron sputtering. Corrosion behavior of Cr-coated SiC and -uncoated SiC coupons was studied by immersing in autoclave (345°C and 16.5 MPa). The weight loss of the Cr coated SiC coupons (3.02% after the 93-days) in the autoclave tests was effectively reduced due to their Cr-coated surfaces, in contrast to the uncoated ones (20.4% after the 78-days). Moreover, microstructural and compositional evolutions were examined by using scanning electron microscopy (SEM), X-ray diffraction (XRD), and Raman spectroscopy. It was revealed that a continuous and dense Cr2O3 layer formed on the surface after the hydrothermal corrosion, which can suppress the in-diffusion of corrosive medium.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.