Epoxy resin is one of the most popular thermosetting resins and has been widely used in many fields for its excellent performance. However, the stable crosslinking structure of waste epoxy (WEP) caused poor interfacial compatibility, which makes it very difficult to be recycled. This paper reported a novel method for recycling the waste epoxy through partial de-crosslinking and recrosslinking processes via solid-state shear milling (S3M). The waste epoxy was effectively pulverized into an ultrafine powder about 17 μm and the crosslinking density decreased from 3.43 × 10 −3 to 2.69 × 10 −3 mol/mL. The C−N, C−C, and C−O−C bonds in the WEP were broken by the mechanochemical action and many hydroxyl and amino groups were formed on the surface of the WEP powder, which could react with the epoxy and curing agent to form the new crosslinking network. The interface strength between the WEP powder and epoxy (EP) resin matrix was improved greatly and there were no voids that could be observed by scanning electron microscopy (SEM) after the re-crosslinking process. The maximum tensile strength, flexural strength, and non-notched impact strength of WEP/EP composites reached up to 42.2 MPa, 73.2 MPa, and 8.8 kJ/ m 2 , which means 62, 41, and 109% enhancement, respectively. This low-cost, high-efficiency, and environmentally friendly method shows great potential for value-added recycling of thermosetting resins.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.