Nanoparticles were proposed as antibacterial cement admixtures for the production of cement-based composites. Nevertheless, the standards for evaluation of such admixtures still do not indicate which model organisms to use, particularly in regard to the further application of material. Apart from the known toxicity of nanomaterials, in the case of cement-based composites there are limitations associated with the mixing and dispersion of nanomaterials. Therefore, four nanooxides (Al2O3, CuO, Fe3O4, and ZnO) and seven microorganisms were tested to initially evaluate the applicability of nanooxides in relation to their further use in cement-based composites. Studies of nanoparticles included chemical analysis, microbial growth kinetics, 4- and 24 h toxicity, and biofilm formation assay. Nanooxides showed toxicity against microorganisms in the used concentration, although the populations were able to re-grow. Furthermore, the effect of action was variable even between strains from the same genus. The effect of nanoparticles on biofilms depended on the used strain. Gathered results show several problems that can occur while studying nanoparticles for specific further application. Proper protocols for nanomaterial dispersion prior the preparation of cement-based composites, as well as a standardized approach for their testing, are the fundamental issues that have to be resolved to produce efficient composites.

No abstract

This contribution investigates the effects of seawater and colloidal silica (NS) in the amounts of 1, 3 and 5 wt%, respectively, on the hydration, strength development and microstructural properties of Portland cement pastes. The data reveal that seawater has an accelerating effect on cement hydration and thus a significant contribution to early strength development was observed. The beneficial effect of seawater was reflected in an improvement in compressive strength for up to 14 days of hydration, while in the 28 days compressive strength values were comparable to that of cement pastes produced with demineralized water. The combination of seawater and NS significantly promotes cement hydration kinetics due to a synergistic effect, resulting in higher calcium hydroxide (CH) production. NS can thus react with the available CH through the pozzolanic reaction and produce more calcium silicate hydrate (C-S-H) gel. A noticeable improvement of strength development, as the result of the synergistic effect of NS and seawater, was therefore observed. In addition, mercury intrusion porosimetry (MIP) tests confirmed significant improvements in microstructure when NS and seawater were combined, resulting in the production of a more compact and dense hardened paste structure. The optimal amount of NS to be mixed with seawater, was found to be 3 wt% of cement.