We demonstrate a tunable bandgap from 2.32 eV to 2.09 eV in phase-pure BiFeO3 by controlling the particle size from 65 nm to 5 nm. Defect states due to oxygen and microstrain show a strong dependence on BiFeO3 particle size and have a significant effect on the shape of absorbance curves. Oxygen-defect induced microstrain and undercoordinated oxygen on the surface of BiFeO3 nanoparticles are demonstrated via HRTEM and XPS studies. Microstrain in the lattice leads to the reduction in rhombohedral distortion of BiFeO3 for particle sizes below 30 nm. The decrease in band gap with decreasing particle size is attributed to the competing effects of microstrain, oxygen defects, and Coulombic interactions.
Cu-deficient graded-zinc Cu-In-Zn-S (CIZS) quantum dots (QDs) were synthesized by a two-step solvothermal method. These CIZS QDs exhibited size and composition tunable photoluminescence characteristics with emission color tunable from greenish-yellow to orange to red with a relatively high quantum yield between 45 and 60%. Novel white-light-emitting (WLE) hybrid composite is fabricated by integrating the blue-emissive 1,4-bis-2-(5-phenyl oxazolyl)-benzene (POPOP) organic fluorophore and quaternary CIZS inorganic QDs. Integrating CIZS QDs with POPOP fluorophore resulted in series of tunable emission colors with CIE coordinates lying in a straight line between the coordinates of the end member. WLE was shown for hybrid mixture comprising 0.5 nM of POPOP and 3 mg/mL of CIZS QDs with color coordinates (0.3312, 0.3324). Thin films of this hybrid mixture in PMMA matrix coated on UV-LED or on glass substrates with UV backlit light also showed broadband WLE with ideal CIE color coordinates of (0.34, 0.33), high color-rendering index value of 92, and correlated color temperature value of 5143 K. The hybrid composite exhibit Forster resonance energy transfer cascading from POPOP to CIZS which results in emission covering the entire visible spectral range. POPOP and CIZS QDs hybrid composite is a versatile material for WLED applications.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.