The aim of the present study was to evaluate the in vitro caries preventive effect of fluoridated orthodontic resins under pH cycling with two types of acid demineralizing saliva. Brackets were bonded to 60 bovine incisors, using either Transbond Plus Color Change (n=30) or Orthodontic Fill Magic (n=30) orthodontic resins. Each group of resin was divided into 3 subgroups (n=10): immersion in remineralizing artificial saliva for 14 days, pH cycling with high cariogenic challenge in acid saliva with pH 5.5, and acid saliva with pH 4.5. After 14 days of pH cycling, the caries preventive effect on the development of white spot lesion was evaluated considering the presence of inhibition zones to white spot lesions using two scores: 0= absence and 1= presence. Kruskal Wallis and Mann-Whitney tests (a=0.05) were used. Formation of white spot lesions was observed only under pH cycling using acid saliva with pH 4.5; with Transbond Plus Color Change being significantly more effective (p<0.05) in preventing the appearance of white spot lesions effect than Orthodontic Fill Magic. The acidity of the demineralizing solution influenced the formation of white spot lesions around orthodontic brackets under highly cariogenic conditions. Transbond Plus Color Change resin presented higher caries preventive effect than Orthodontic Fill Magic.

The aim of this study is to assess the in vitro shear bond strength and adhesive remnant index (ARI) of one and two-step fluoridated orthodontic resins under conditions that simulate high cariogenic challenge. Edgewise brackets for maxillary central incisors were randomly bonded to 80 bovine incisors, using either Transbond TM Plus Color Change orthodontic resin and a self-etching primer adhesive (G1; n = 40) or Orthodontic Fill Magic with a conventional acid-etch technique (G2; n = 40). Each group of resin (n = 10) was divided into: immediate shear (A-pre-cycling control), immersion in artificial remineralizing saliva (neutral saliva) for 14 days (B-post-cycling control) and pH cycling with high cariogenic challenge (C-acid saliva with pH 5.5 and D-acid saliva with pH 4.5). After 14 days of pH cycling, the shear bond strength and ARI were evaluated. Considering the shear bond strength, Transbond TM Plus Color Change resin was stronger than Orthodontic Fill Magic when it was submitted to high cariogenic challenge (p < 0.05). Also Transbond TM Plus Color Change resin showed better adhesion to enamel than Orthodontic Fill Magic, in all situations evaluated (p < 0.05). It could be concluded that Transbond TM Plus Color Change resin presented better shear bond strength and adhesive remnant index when submitted to high cariogenic challenge, in comparison with Orthodontic Fill Magic.

The aim of the present study was to evaluate the effect of fluoride in prevention of tooth erosion around orthodontic brackets under erosive challenge. Edgewise brackets were bonded with Transbond™ XT composite on vestibular surface of 40 bovine incisors. The teeth were assigned to 4 groups (n=10): G1: Remineralizing saliva; G2: Erosive challenge; G3: Experimental group submitted to topical application of neutral fluoride gel (2% NaF) before erosive challenge; G4: Experimental group submitted to three daily applications of fluoride dentifrice (PFM 1500 ppmF) during erosive challenge. After 14 days of erosive challenge, direct visual and tactile examination were performed by two calibrated and trained examiners (Kappa = 0.867). The following scores were used: 0 = Intact enamel, 1 = Demineralized enamel without cavity, 2 = Demineralized enamel with cavity, 3 = Remineralized enamel without cavity, 4 = Remineralized enamel with cavity. Kruskal-Wallis and Mann-Whitney tests were applied to determine erosion levels, establishing a confidence interval of 95% (p<0.05). G2 and G3 presented 100% of score 2, with large cavities, presenting rough and opaque surface. G4 showed 50% of score 3 and 50% of score 4. Considering the studied conditions, it was found a significant difference between G2 and G4 and between G3 and G4 (p<0.01). By contrast to single application of neutral fluoride gel, the high frequency of use of fluoride at low concentration had a great influence during the dynamics of erosion.