SUMMARY: A series of "combined" liquid crystal (LC) polyesters consisting of aromatic main-chain backbones and flexible aliphatic side chains with 4-cyanobiphenyl end groups was synthesized based on the polycondensation of 2,29-bis(trifluoromethyl)-4,49-biphenyldicarbonyl chloride with 2,29-bis{x-[4-(4-cyanophenyl)phenoxy]-n-alkoxycarbonyl]}-4,49-biphenyldiol (PEFBP). In a recent study of PEFBP(n = 11) containing eleven methylene units in the side chains, four different phases were identified in addition to the isotropic melt (I). They are as follows: an orthorhombic crystalline (K O ) phase, two triclinic crystalline (K T1 and K T2 ) phases in the high temperature region, and a nematic (N) phase. In this report, we focus on the even-odd effect of the methylene units in the side chains on the phase structure and transition behavior of PEFBP(n = 8, 9, 10 and 11)s. Two even-numbered PEFBPs with either eight or ten methylene units in the side chains [PEFBP(n = 10 and 8)s] were studied. An odd-numbered PEFBP containing nine methylene units, PEFBP(n = 9), was also investigated in addition to PEFBP(n = 11) which was reported on previously 1,2) . It was found that both of the PEFBPs with even-numbered methylene units in their side chains [PEFBP(n = 10 and 8)s] exhibit only a nematic and a smectic A (S A ) phase. Their phase transition sequence during heating and cooling is T g (S A LC glass) e E S A e E N e E I Since only LC phases exist, this is a thermodynamically reversible transition sequence independent upon thermal history. For PEFBP(n = 9 and 11)s, crystalline phases with three-dimensional order are observed above the NLC glass transition temperature in addition to the N phase. In PEFBP(n = 9), the N and K O phases are similar to those seen in the case of PEFBP(n = 11). However, this polymer presents only one triclinic crystalline phase, while two triclinic crystal phases are observed in PEFBP(n = 11). The phase transition sequence in these odd-numbered PEFBPs during heating between 2.5 8C/min -10 8C/min for a sample cooled from the isotropic melt at the same rate isNevertheless, this sequence does not represent a case of thermodynamic equilibrium. The K O and K T (s) phases in PEFBP(n = 9 and 11)s and the S A phase in PEBFP(n = 8 and 10)s are characteristics of the evenodd effect observed in this series of combined LC polyesters. The number of methylene units in the side chains thus plays a critical role in the formation of phase order and transition behavior in a way quite different from the common even-odd effect seen in main-chain LC polymers. Furthermore, this effect also indicates that the 4-cyanobiphenyl groups in the side chains are incorporated with the main-chain backbones to form the liquid crystal and crystal phases.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.