Titanium Grade 4 (Ti G4) is the most commonly used material for dental implants due to its excellent mechanical properties, chemical stability and biocompatibility. A thin, self-passive oxide layer with protective properties to corrosion is formed on its surface. However, the spontaneous TiO2 layer is chemically unstable. In this work, the impact of autoclaving time on corrosion resistance of Ti G4 in artificial saliva solution with pH = 7.4 at 37 °C was studied. Ti G4 was sandblasted with white Al2O3 particles and autoclaved for 30–120 min. SEM, EDS, 2D roughness profiles, confocal laser scanning microscopy, and a Kelvin scanning probe were used for the surface characterization of the Ti G4 under study. In vitro corrosion resistance tests were conducted using open circuit potential, polarization curves, and electrochemical impedance spectroscopy measurements. It was found that Sa parameter, electron work function, and thickness of the oxide layers, determined based on impedance measurements, increased after autoclaving. The capacitive behavior and high corrosion resistance of tested materials were revealed. The improvement in the corrosion resistance after autoclaving was due to the presence of oxide layers with high chemical stability. The optimal Ti G4 surface for dentistry can be obtained by sandblasting with Al2O3 with an average grain size of 53 µm, followed by autoclaving for 90 min.

No abstract

This work concerns the development of a method of functionalization of the surface of the biomedical Ti–6Al–7Nb alloy by producing oxide nanotubes (ONTs) with drug-eluting properties. Shaping of the morphology, microstructure, and thickness of the oxide layer was carried out by anodization in an aqueous solution of 1 M ethylene glycol with the addition of 0.2 M NH4F in the voltage range 5–100 V for 15–60 min at room temperature. The characterization of the physicochemical properties of the obtained ONTs was performed using SEM, XPS, and EDAX methods. ONTs have been shown to be composed mainly of TiO2, Al2O3, and Nb2O5. Single-walled ONTs with the largest specific surface area of 600 cm2 cm−2 can be obtained by anodization at 50 V for 60 min. The mechanism of ONT formation on the Ti–6Al–7Nb alloy was studied in detail. Gentamicin sulfate loaded into ONTs was studied using FTIR, TG, DTA, and DTG methods. Drug release kinetics was determined by UV–Vis spectrophotometry. The obtained ONTs can be proposed for use in modern implantology as carriers for drugs delivered locally in inflammatory conditions.

Titanium Grade 4 (Ti G4) is widely used in medicine for dental implants. The failure-free life of implants depends on their properties such as resistance to wear and friction processes. This paper presents an analysis of the influence of sandblasting on tribological wear of commercial dental implants made of TiG4 in artificial saliva. Tribological wear measurements were performed in a reciprocating motion in the ball-on-disc system. The scanning electron microscopy/energy-dispersive X-ray spectroscopy (SEM/EDS) method was used to characterize the surface of the implants before and after the tribological wear test. The microhardness of Ti G4 was measured before and after sandblasting by the Vickers method. The contact angle was determined by the method of sitting drop in air. The residual stress test using the X-Ray Diffraction (XRD) single-{hkl} sin2ψ method was carried out. The compressive residual stress of 324(7) MPa and surface hardening of Ti G4 was revealed after sandblasting with Al2O3 particles of 53–75 μm in diameter. It was found that sandblasting changes the surface wettability of Ti G4. The intermediate wettability of the mechanically polished surface and the hydrophobicity of the sandblasted surface was revealed. Sandblasting reduces the tribological wear and friction coefficient of Ti G4 surface in saliva. The three-body abrasion wear mechanism was proposed to explain the tribological wear of Ti G4 in saliva.

Calcium phosphate coatings are able to improve the osseointegration process due to their chemical composition, which is similar to that of bone tissues. In this work, to increase the long-term corrosion resistance and to improve the osseointegration process of commercially pure titanium Grade 4 (CpTi G4), biomimetic amorphous calcium phosphate (ACP) coatings were electrodeposited for the first time from an acetate bath with a pH level of 7.0 and a Ca:P ratio of 1.67. ACP coatings were obtained on CpTi G4 substrate subjected to sandblasting and autoclaving using electrochemically assisted deposition at a potential of −3 V relative to the open circuit potential for 30 min at room temperature. SEM, EDS, 2D roughness profiles, amplitude-sensitive eddy current method, and Kelvin scanning probe were used for the surface characterization of the biomaterial under study. In vitro corrosion resistance tests were conducted for 21 days in artificial saliva using open circuit potential, polarization curves, and electrochemical impedance spectroscopy measurements. The passive-transpassive behavior was revealed for the obtained ACP coatings. The long-term corrosion resistance test showed a deterioration of the protective properties for CpTi G4 uncoated and coated with ACP with immersion time. The mechanism and kinetics of the pitting corrosion on the CpTi G4|TiO2|ACP coating system are discussed in detail.