We synthesize polybase brushes and investigate their swelling behavior. Poly(2-(dimethylamino)ethyl methacrylate)) (PDMAEMA) brushes are prepared by the "grafting from" method using surface-initiated Atom Transfer Radical Polymerization to obtain dense brushes with relatively monodisperse chains (PDI = 1.35). In situ quaternization reaction can be performed to obtain poly(2-(trimethylamino)ethyl methacrylate)) (PTMAEMA) brushes. We determine the swollen thickness of the brushes using ellipsometry and neutron reflectivity techniques. Brushes are submitted to different solvent conditions to be investigated as neutral brushes and weak and strong polyelectrolyte brushes. The swelling of the brushes is systematically compared to scaling models. It should be pointed out that the scaling analysis of different types of brushes (neutral polymer and weak and strong polyelectrolyte brushes) is performed with identical samples. The scaling behavior of the PDMAEMA brush in methanol and the PTMAEMA brush in water is in good agreement with the predicted scaling laws for a neutral polymer brush in a good solvent and a polyelectrolyte brush in the osmotic regime. The salt-induced contraction of the quaternized brush is observed for high salt concentration, in agreement with the predicted transition between the regimes of the osmotic brush and the salted brush. From the crossover concentration, we calculate the effective charge ratio of the brush following the Manning counterion condensation. We also use PDMAEMA brushes as pH-responsive polybase brushes. The swelling behavior of the polybase brush is intermediate with respect to the behavior of the neutral polymer brush in a good solvent and the behavior of the quenched polyelectrolyte brush, as expected. The effective charge ratio of the PDMAEMA brush is determined as a function of pH using the scaling law of the polyelectrolyte brush in the osmotic regime.

No abstract

Highly monodisperse poly(N-isopropylacrylamide), PNiPAM, microgels were prepared by the conventional radical polymerization of NiPAM in the presence of dimethylamino ethyl methacrylate (DMAEMA) monomers at various concentrations. The effect of DMAEMA on the polymerization of PNiPAM microgels was examined at constant initiator (V50) and cross-linker (MBA) concentrations. The presence of DMAEMA in the synthesis batch allows for the preparation of PNiPAM microgels with controlled size and a narrow size distribution. The oil(dodecane)/water interfacial properties of the model PNiPAM microgels were then investigated. The pendant drop technique was used to measure the interfacial tensions as a function of temperature. Over the whole range of temperature (20-45 degrees C), the interfacial tension remains low (on the order of 17 mN/m) and goes through a minimum (12 mN/m) at a temperature of about 34 degrees C, which well matches the volume phase transition temperature (VPTT) of PNiPAM microgels. Below the VPTT, the decrease in the interfacial tension with temperature is likely to be due to the adsorption of dense layers because of the decrease of the excluded volume interactions. Above the VPTT, we suggest that the increase in the interfacial tension with temperature comes from the adsorption of loosely packed PNiPAM microgels. We also studied the effect of temperature on the stability of emulsions. Dodecane in water emulsions, which form at ambient temperature, are destabilized as the temperature exceeds the VPTT. In light of the interfacial tension results, we suggest that emulsion destabilization arises from the adsorption of aggregates above the VPTT and not from an important desorption of microgels. Aggregate adsorption would bring a sufficiently high number of dodecane molecules into contact with water to induce coalescence without changing the interfacial tension very much.