Samarium (III) (Sm)-based conversion layer was developed on carbon steel for improvement of the epoxy coating adhesion properties, corrosion protection performance, and cathodic delamination resistance. The post-heating and pre-heating actions impact on the Sm (III) film properties was studied. The morphology and chemistry of the Sm (III) film were examined by scanning electron microscopy, atomic force microscopy, contact angle, and X-ray photoelectron spectroscopy. The outcomes from these analyses proved that both pre-heating and post-heating actions altered the morphology and chemistry of the Sm (III) film. The pull-off test indicated that Sm (III) film could enhance the adhesion between the epoxy/steel through increasing the surface roughness and enhancing the surface free energy. The improvement in adhesion strength led to a decrease in the cathodic delamination rate up to 78%. Although both pre-heating and post-heating actions improved the corrosion protection performance of the epoxy film, the pre-heating method had a much higher impact on the epoxy film corrosion resistance enhancement. An excellent corrosion protective performance was observed in the samples preheated at 65°C after 1000 h exposure to salt spray test.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.