This study investigated the effect of chitosan particle sizes on the properties of carboxymethyl chitosan (CMCh) powders and films. Chitosan powders with different particle sizes (75, 125, 250, 450 and 850 µm) were used to synthesize the CMCh powders. The yield, degree of substitution (DS), and water solubility of the CMCh powders were then determined. The CMCh films prepared with CMCh based on chitosan with different particle sizes were fabricated by a solution casting technique. The water solubility, mechanical properties, and water vapor transmission rate (WVTR) of the CMCh films were measured. As the chitosan particle size decreased, the yield, DS, and water solubility of the synthesized CMCh powders increased. The increase in water solubility was due to an increase in the polarity of the CMCh powder, from a higher conversion of chitosan into CMCh. In addition, the higher conversion of chitosan was also related to a higher surface area in the substitution reaction provided by chitosan powder with a smaller particle size. As the particle size of chitosan decreased, the tensile strength, elongation at break, and WVTR of the CMCh films increased. This study demonstrated that a greater improvement in water solubility of the CMCh powders and films can be achieved by using chitosan powder with a smaller size.

The effect of argon (Ar) and oxygen (O2) gases as well as the treatment times on the properties of modified bamboo fibers using dielectric barrier discharge (DBD) plasma at generated power of 180 W were investigated. The plasma treatment of bamboo fibers with inert gases leads to the generation of ions and radicals on the fiber surface. Fourier transform-infrared spectroscopy (FTIR) confirmed that the functional groups of lignin and hemicellulose were reduced owing to the removal of the amorphous portion of the fibers by plasma etching. X-ray diffraction analysis (XRD) results in an increased crystallinity percentage. X-ray photoelectron spectroscopy (XPS) results showed the oxygen/carbon (O/C) atomic concentration ratio increased with increasing treatment time. The fiber weight loss percentage increased with increased treatment time. Scanning electron microscopy (SEM) images showed that partial etching of the fiber surface led to a higher surface roughness and area and that the Ar + O2 gas plasma treatment provided more surface etching than the Ar gas treatment because of the oxidation reaction of the O2 plasma. The mechanical properties of fiber-reinforced epoxy (FRE) matrix composites revealed that the F(tr)RE-Ar (30) samples showed a high tensile strength, whereas the mechanical properties of the F(tr)RE-Ar + O2 sample decreased with increased treatment time.

The pulsed electric field (PEF) was applied to improve the extraction yield and properties of rice bran proteins from two rice varieties (“Kum Chao Mor Chor 107” and “Kum Doi Saket”). As compared to the conventional alkaline extraction, PEF treatment at 2.3 kV for 25 min increased the protein extraction efficiency by 20.71–22.8% (p < 0.05). The molecular weight distribution detected by SDS-PAGE and amino acid profiles of extracted rice bran proteins was likely unchanged. The PEF treatment influenced changes in the secondary structures of rice bran proteins, especially from the β-turn to the β-sheet structure. Functional properties of rice bran protein including oil holding capacity and emulsifying properties were significantly improved by PEF treatments by about 20.29–22.64% and 3.3–12.0% (p < 0.05), respectively. Foaming ability and foam stability increased by 1.8- to 2.9-fold. Moreover, the in vitro digestibility of protein was also enhanced, which was consistent with the increment of DPPH and ABTS radical-scavenging activities of peptides generated under in vitro gastrointestinal digestion (37.84–40.45% and 28.46–37.86%, respectively). In conclusion, the PEF process could be a novel technique for assisting the extraction and modification of the protein’s digestibility and functional properties.

No abstract