Polyvinylpyrrolidone (PVP)-capped Pt nanoparticles (NPs) were synthesized in mostly tetrahedral (TH-Pt, [edge] = 4.3 ± 0.7 nm) or spherical (S-Pt, [d] = 3.4 ± 0.8 nm) shapes and assembled layer-by-layer in poly(diallyldimethylammonium) chloride on electrodes driven by electrostatic and hydrophobic interactions. The nanostructured Pt electrodes were characterized using hydrogen underpotential deposition (H(upd)) in 1 M H2SO4. The H(upd) charge increased linearly with the PDDA-Pt NP adsorption cycle measured up to 10 cycles revealing a linear incorporation of Pt NPs per cycle, indicative of reproducible surface charge reversal despite the submonolayer NP coverage imaged by TEM on a PDDA layer, and showing the feasibility of charge and mass transport in the thickness of the films. H(upd) at both PVP-TH-Pt and PVP-S-Pt occurred in two states, a major weak-adsorption H(W) peak, and a minor strong-adsorption state H(S) appearing as a shoulder. H(upd) features and other electrochemical processes at assemblies of PVP-Pt NP in PDDA were compared to assemblies of 2.5 nm polyacrylate-capped Pt NPs in PDDA and to polycrystalline Pt. Results indicated that H(W) adsorption likely occurs on a PVP-modified Pt NP surface without being accompanied by PVP desorption, while H(S) occurs on free (100) sites. The PVP-Pt NPs were resistant to surface oxidation and were stable against usual surface restructuring when scanned into the Pt-oxide potential region as they remained modified with PVP. O2 evolution was also suppressed by PVP-capping compared to PAC-Pt NPs and polycryst-Pt, but the assemblies were electrocatalytic for hydrogen evolution, hydrogen oxidation, and oxygen reduction. Increasing anodic polarization increased the H(W) charge but without causing a potential shift, indicating absence of PVP decapping or Pt surface restructuring, but possibly some structural polymer rearrangement increasing the accessibility of buried sites for H-adsorption.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.