Electrospinning is a valuable technology for cartilage tissue engineering (CTE) due to its ability to produce fibrous scaffolds mimicking the nanoscale and alignment of collagen fibers present within the superficial zone of articular cartilage. Coaxial electrospinning allows the fabrication of coreshell fibers able to incorporate and release bioactive molecules (e.g., drugs or growth factors) in a controlled manner. Herein, we used coaxial electrospinning to produce coaxial poly(glycerol sebacate) (PGS)/poly(caprolactone) (PCL) aligned nanofibers (core:PGS/shell:PCL). The obtained scaffolds were characterized in terms of their structure, chemical composition, thermal properties, mechanical performance and in vitro degradation kinetics, in comparison to monoaxial PCL aligned fibers and respective non-aligned controls. All the electrospun scaffolds produced presented average fiber diameters within the nanometer-scale and the core-shell structure of the composite fibers was clearly confirmed by TEM. Additionally, fiber alignment significantly increased (>2-fold) the elastic modulus of both coaxial and monoxial scaffolds. Kartogenin (KGN), a small molecule known to promote mesenchymal stem/stromal cells (MSC)
Designing biodegradable scaffolds with bone-compatible mechanical properties has been a significant challenge in the field of bone tissue engineering and regenerative engineering. The objective of this work is to improve the polymeric scaffold's mechanical strength by compositing it with mechanically superior carbon nanotubes. Poly(lactide-co-glycolide) (PLGA) microsphere scaffolds exhibit mechanical properties in the range of human cancellous bone. On the other hand, carbon nanotubes have outstanding mechanical properties. The aim of this study is to improve further the mechanical strength of PLGA scaffolds such that they may be applicable for a wide range of load-bearing repair and regeneration applications. We have formed composite microspheres of PLGA containing pristine and modified (with hydroxyl (OH), carboxylic acid (COOH)) multi-walled carbon nanotubes (MWCNTs), and fabricated them into three-dimensional porous scaffolds. Results show that by adding only 3% MWCNTs, the compressive strength and modulus was significantly increased (35 MPa, 510.99 MPa) compared to pure PLGA scaffolds (19 MPa and 166.38 MPa). Scanning electron microscopy images showed excellent cell adhesion and proliferation. In vitro studies exhibited good cell viability, proliferation and mineralization. The in vivo study, however, indicated differences in inflammatory response throughout the 12 weeks of implantation, with OH-modified MWCNTs having the least response, followed by unmodified and COOH-modified exhibiting a more pronounced response. Overall, our results show that PLGA scaffolds containing water-dispersible MWCNTs are mechanically stronger and display good cellular and tissue compatibility, and hence are potential candidates for load-bearing bone tissue engineering.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.