An attempt to improve the machining performance of NbC-Ni cutting inserts by rapid pulse electric current sintering (PECS), TiC and Mo 2 C additions and laser surface modification (LSM) was done. Use of a nickel binder and additions TiC and Mo 2 C to liquid phase sintered (LPS) NbC based samples led to comparable hardness (> 13 GPa) and K IC (~10 MPa.m 1/2 ) to LPS WC-Co/Ni samples. The laser surface modification (LSM) technique produced a~2.5 μm thick self-carbide coating, increasing the surface hardness of all the samples. Laser surface modification was done to improve abrasion and attrition wear resistance. Face-milling of grade 17 grey cast iron (BS 1452/GG35) was conducted at 100-500 m/min cutting speeds (v c ) and 0.25-1.5 mm depths of cut (a p ). The insert wear was measured after every pass, and analyzed by annular dark field scanning transmission electron microscopy (ADF-STEM). During roughing, WC-Co based inserts had the lowest flank wear rate (FWR) values, with the WC-10Co (LPS) insert having a FWR of 10.15 μm/min after 20 min cutting time. However, during semifinishing and finishing, NbC-4TiC-12Ni (PECS) and NbC-4Mo 2 C-4TiC-12Ni (PECS) inserts had the lowest FWR values, showing up to six times longer tool life than the WC-Co (LPS) inserts based inserts and 12 times longer life than the WC-Ni based inserts. Generally, LSM improved the NbC inserts' tool life, reducing the FWR values in all NbC based inserts in all cutting tests.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.