The present study deals with the short fatigue crack growth behaviour of a ferritic steel (nuclear grade SA 333 Grade 6 steel) weld metal at two load ratios R of 0.1 and –1. Single edge notched weld joint specimens were tested at different stress levels. The acceleration and deceleration in short crack growth with increasing stress intensity factor range was explained in terms of microstructure of weld metal. Acicular ferrite and grain boundary ferrite acted as barriers to crack growth. Non-propagating cracks were observed due to multiple cracks and blocking by ferrite grain boundaries. Transition crack length, the limiting crack length above which the crack exhibited a typical long crack behaviour, was determined to be 1 mm at R=0.1 and 1.5 mm at R=2 1.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.