Co 80 Pt 20 thin films on Cr, Cr80V20, or Cr90Ti10 underlayers were studied to improve the magnetic properties for permanent magnetic stabilization layer application in anistropic magnetoresistance/giant magnetoresistance devices. A significant improvement of nearly 15% in coercivity was achieved for CoPt films on CrTi underlayer, when compared to either Cr or CrV underlayer. X-ray diffraction pattern analysis showed that CrTi underlayer increased the intensity of CoPt (10.0) indicating enhanced crystallographic in-plane texture. With CrTi underlayer, CoPt coercivity increased linearly as Mrt was reduced from 4.3 to as low as 0.4 memu/cm2. The squareness and S* values started to drop sharply when the Mrt of CoPt film decreased to below 1.0 memu/cm2. In addition to 15% higher coercivity, another important property of CrTi/CoPt was that for CrTi underlayer thickness between 3 and 20 nm very little change in the coercivity, squareness, and S* of CoPt layer was observed. The CoPt films showed excellent corrosion resistance towards high humidity and good thermal stability up to 300 °C. The CoPt films with the underlayer of CrTi and CrV showed slightly less corrosion resistance towards industrial pollutants than those with no underlayer and Cr underlayer.

No abstract available.

Articles you may be interested inEffect of deposition interruption and substrate bias on the structure of sputter-deposited yttria-stabilized zirconia thin films Deposition and properties of yttriastabilized zirconia thin films using reactive direct current magnetron sputtering J. Vac. Sci. Technol. A 9, 3054 (1991); 10.1116/1.577172Wear properties of yttriastabilized hafnia overcoats (abstract)