This article aims to prepare by injection molding recycled polymeric composites based on PA66 reinforced with short carbon fibers after artificial aging for applications in the automotive field. The aging cycles involves the combined action of UV radiation, moisture, and temperature in order to simulate the common outdoor conditions. The 100% recycled composites are obtained by the regranulation of the aged specimens followed by the remelting and re-injection molding. The study is focused on the comparison between the mechanical behavior and the microstructure of the composites before and after mechanical recycling. The results of mechanical, thermal, and morphological investigations reveal that the recycling process had no significant effect on the final properties and microstructure of the recycled composites. Therefore the recycled PA66CF30 composites could be successfully used for structural or semi-structural automotive applications guaranteeing good final performances and advantages from the environmental point of view.

No abstract

No abstract

No abstract

No abstract

A High Power Impulse Magnetron Sputtering (HiPIMS) method for depositing TiAlN environmental barrier coatings on the surface of Ti-48Al-2Cr-2Nb alloy was developed in view of their exploitation in turbine engines. Three differently engineered TiAlN films were processed and their performance compared. Bare intermetallic alloy coupons and coated specimens were submitted to thermal cycling under oxidizing atmosphere up to 850 °C or 950 °C, at high heating and cooling rates. For this purpose, a burner rig able to simulate the operating conditions of the different stages of turbine engines was used. Microstructures of the samples were compared before and after each test using several techniques (microscopy, XRD, and XPS). Coating-intermetallic substrate adhesion and tribological properties were investigated too. All the TiAlN films provided a remarkable increase in oxidation resistance. Good adhesion properties were observed even after repeated thermal shocks. HiPIMS pretreatments of the substrate surfaces performed before the coating deposition significantly affected the oxidation rate, the oxide layer composition and the coating/substrate adhesion.

No abstract