The bauxite mineral obtained from Araku, Vishakapatnam district of Andhra Pradesh, India is used in the present work. Structural characterization was performed by X-ray diffraction (XRD). The mineral was found to be gibbsite in phase. The transitional metal ions present were investigated using electron paramagnetic resonance (EPR) and optical absorption spectra. The EPR results suggest that Fe 3+ has replaced Al 3+ in the unit cell of bauxite. The optical absorption spectrum is due to Fe 3+ which indicates that it is in distorted octahedral environment. The near-infrared (NIR) spectrum is due to water fundamentals and combination overtones, which confirm the formula of the compound. The impurities in the mineral are identified using spectroscopic techniques.

Copper doped zinc aluminum ferrites CuxZn1-x.(AlxFe2-x)O4 are synthesized by the solid-state reaction route and characterized by XRD, TEM, EPR and non linear optical spectroscopy techniques. The average particle size is found to be from 35 to 90nm and the unit cell parameter "a" is calculated as from 8.39 to 8.89Å. The cation distributions are estimated from X-ray diffraction intensities of various planes. The XRD studies have verified the quality of the synthesis of compounds and have shown the differences in the positions of the diffraction peaks due to the change in concentration of copper ions. TEM pictures clearly indicating that fundamental unit is composed of octahedral and tetrahedral blocks and joined strongly. The selected area electron diffraction (SAED) of the ferrite system shows best crystallinity is obtained when Cu content is very. Some of the d-plane spacings are exactly coinciding with XRD values. EPR spectra is compositional dependent at lower Al/Cu concentration EPR spectra is due to Fe(3+) and at a higher content of Al/Cu the EPR spectra is due to Cu(2+). Absence of EPR spectra at room temperature indicates that the sample is perfectly ferromagnetic. EPR results at low temperature indicate that the sample is paramagnetic, and that copper is placed in the tetragonal elongation (B) site with magnetically non-equivalent ions in the unit cell having strong exchange coupling between them. This property is useful in industrial applications. Nonlinear optical properties of the samples studied using 5ns laser pulses at 532nm employing the open aperture z-scan technique indicate that these ferrites are potential candidates for optical limiting applications.