This work focuses on investigating the curing process of an epoxy-based resin—Aerotuf 275-34TM, designed for aerospace applications. To study the curing degree of Aerotuf 275-34TM under processing conditions, woven carbon fiber fabric (WCFF)/Aerotuf 275-34TM composite laminates were produced by compression molding using different processing temperatures (110, 135, 160, and 200 °C) during 15 and 30 min. Then, the mechanical behavior of the composite laminates was evaluated by tensile tests and correlated to the resin curing degree through Fourier-transform infrared spectroscopy (FTIR) analysis. The results show the occurrence of two independent reactions based on the consumption of epoxide groups and maleimide (MI) double bonds. In terms of epoxide groups, a conversion degree of 0.91 was obtained for the composite cured at 160 °C during 15 min, while the measured tensile properties of [±45°] WCFF/Aerotuf 275-34TM laminates confirmed that these epoxy resin curing processing conditions lead to an enhancement of the composite mechanical properties.
Stress shielding is a well-known failure factor in hip implants. This work proposes a design concept for hip implants, using a combination of metallic stem with a polymer coating (polyether ether ketone (PEEK)). The proposed design concept is simulated using titanium alloy stems and PEEK coatings with thicknesses varying from 100 to 400 μm. The Finite Element analysis of the cancellous bone surrounding the implant shows promising results. The effective von Mises stress increases between 81 and 92% for the complete volume of cancellous bone. When focusing on the proximal zone of the implant, the increased stress transmission to the cancellous bone reaches between 47 and 60%. This increment in load transferred to the bone can influence mineral bone loss due to stress shielding, minimizing such effect, and thus prolonging implant lifespan.
This article focuses on studying the rheological behavior of isotropic and anisotropic magnetorheological elastomers (MREs), made of carbonyl iron microparticles dispersed into a silicone–rubber matrix by considering 20 and 30 wt % of microparticles. Sample sets were prepared for each composition, with and without the application of an external magnetic field. Experimental measurements of the material rheology behavior were carried out by a shear oscillatory rheometer at constant temperature, to determine both the shear storage modulus (G′) and shear loss modulus (G′′) for all characterized samples. Then, experimental data collected from the isotropic and the anisotropic material samples were used to plot the Cole-Cole diagrams to quantify the interfacial adhesion between carbonyl iron microparticles and the silicone-rubber matrix. Furthermore, the Fractional Zener Model (FZM) with two spring-pots in series is used for quantitative analysis of collected experimental data.
The enhanced cubication method is applied to develop approximate solutions for the most common nonlinear oscillators found in the literature. It is shown that this procedure leads to amplitude-time response curves and angular frequency values with maximum relative errors lower than those found by previously developed approximate solutions.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.