A hot press process was used as a technique to pound a polyamide type of polymer of a thickness (2mm) to stainless steel AISI 316L of the thickness (1mm). A hybrid joint of dissimilar material was accomplished by a hot press bonding process. During the joining process, three different parameters of process were used: processing temperature of 175, 170 and 165°C, processing pressure of 3, 6 and 9 bar and time of 1.5, 3 and 4.5 min. The surface of stainless steel was prepared and treated by a mechanical treatment (surface grinding) to improve the wettability to increase the shear strength. A shear tensile, scanning electron microscope (SEM) and energy dispersive spectrometry (EDS) tests were used to investigate and examine the joint (bounding) specimens. The Minitab program was used to analyze the effect of the parameters of the joining process on the joint properties. The maximum and minimum values of shear force are exhibited at a processing temperature of 165°C, applied pressure of 6 bars and processing time of 1.5 minutes; the minimum shear force was found to be 675 N, while the maximum shear force was 2182 N at a processing temperature of 175°C, applied pressure of 6 bars and processing time of 3 minutes. The tested joints failed by an interfacial shear and necking in the polymer side with a ductile fracture. The joining process occurred through a mechanical interlocking between the molten polymer and the treated surface of the steel specimen. The average thickness of the joining line for the tested specimens was 8µm.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.