The objective of this work is to improve the structural characteristics of hollow glass microsphere (HGM) filled epoxy syntactic foam composites with little voids content and improved HGM dispersion in the composite. A modified degassing technique has been introduced during resin casting process of the HGM filled syntactic foam composites. The effect of HGM content volume fractions (5–25%) on the degassing techniques was examined. The syntactic foam composites were characterized by analysing structural morphology using Scanning Electron Microscopy (SEM), Transmission Electron Microscopy(TEM), and density measurements (theoretical and experimental). Less than 5% void content has been achieved in this study. This resulted in improved tensile and dynamic mechanical properties (DMA).
Epoxy syntactic foams (SF) filled with hollow glass microspheres (HGM) were prepared by simple resin casting method and characterization in this study. The effect of varying the amount of HGM on the specific mechanical and water absorption properties of SF composites were investigated. Five different composition of SF (SFT60-0.5 to SFT60-2.5) were compared with the neat epoxy matrix. The wall thickness of the microballoons differ because of its different percentile size distribution (10th, 50th and 90th), which reflects in its density variation. The results show that the specific tensile and flexural strength increases with an increasing filler (HGM) content. The density of SF filled with HGM reduces with increasing volume fraction of filler content. Scanning electron microscopy was done on the failed samples to examine the fractured surfaces. The water absorption capacity of the SF was also investigated as it relates to the HGM volume fraction variation. All the syntactic foam composition shows a better diffusion coefficient capacity than the neat epoxy resin. This makes it applicable in structural purposes and several marine application products such as Autonomous Ultimately Vehicle (AUV).
SUMMARYStudies on the spleen in Nigerians are rare. This study reviewed retrospectively the gross and histopathological findings in spleens received at the histopathology laboratory of the Obafemi Awolowo University Hospital (OAUTHC), Ile-Ife, Nigeria. 119 consecutive splenectomy specimens received within a period of 18 years were analysed with respect to age, sex, pathological diagnoses and indication for splenectomy. There were 76 males and 43 females with a mean age of 34.8 years (STD 19.6 years). Spleen weight, size, the presence of malarial parasite as well as fibrosis was not documented in many cases. The most frequent finding both grossly and microscopically was haemorrhagic necrosis from laceration of the spleen arising from trauma (62.7% of all cases). Road traffic accident (RTA) accounted for 86% of all trauma cases and was the predominant finding in both sexes up to the age of 50 years. Thereafter, haematological malignancy was the predominant finding in the spleen. Chronic lymphocytic leukaemia (CLL) was the most common haematological malignancy in the spleen. The indications for splenectomy correlated well with the histological findings (kappa=0.81). Pathological description of spleen specimens is inadequate. Trauma is the major reason for splenectomy. In elderly Nigerians, splenectomy specimen would likely show CLL.
A solution casting approach is used to create hollow glass microsphere (HGM)-filled epoxy–syntactic foam composites (e–SFCs) by varying the concentrations of HGM in epoxy according to different particle sizes. Density analysis is used to investigate the impact of concentration and particle size regularity on the microstructure of e-SFCs. It was observed that e–SFCs filled with an HGM of uniform particle sizes exhibit a reduction in density with increasing HGM concentration, whereas e-SFCs filled with heterogeneous sizes of HGM exhibit closeness in density values regardless of HGM concentration. The variation in e–SFC density can be related to HGM packing efficiency within e–SFCs in terms of concentration and particle size regularity. The particle size with lowest true density of 0.5529 g/cm3, experimental density of 0.949 g/cm3 and tensile strength of 55.74 MPa resulted in e-SFCs with highest specific properties of 100.81 (MPa·g/cm3), with a 35.1% increase from the lowest value of 74.64 (MPa·g/cm3) at a true density of 0.7286 g/cm3, experimental density of 0.928 g/cm3 and tensile strength of 54.38 MPa. The e–SFCs’ theoretical density values were obtained. The variance in theoretical and experimental density values provides a thorough grasp of packing efficiency and inter-particle features.
Syntactic foam made from hollow glass microspheres (HGM) in an epoxy matrix has proven to be a good material with a strong structural strength. Understanding filler particle size variation is important in composite material formation, especially in syntactic foam, because of its numerous applications such as aerospace, marine, and structural purposes. In this present work, the effects of particle variation in different sizes (20–24 µm, 25–44 µm, 45–49 µm, and 50–60 µm) on the mechanical properties of the syntactic foam composites with a focus on flexural strength, modulus, and fracture surfaces are investigated. The particle sizes are varied into five volume fractions (5, 10, 15, 20, and 25 vol%). The results show that the highest flexural strength is 89 MPa at a 5 vol% fraction of 50–60 µm particle size variation with a 69% increase over the neat epoxy. This implies that the incorporation of HGM filler volume fraction and size variation has a strong effect on the flexural strength and bending modulus of syntactic foam. The highest particle size distribution is 31.02 at 25–44 µm. The storage modulus E’ increased at 30 °C, 50 °C, and 60 °C by 3.2%, 47%, and 96%, respectively. The effects of wall thickness and aspect ratio on the size of the microstructure, the fracture surfaces, and the viscoelastic properties are determined and reported accordingly.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.