We address two aspects of general interest for the chemical synthesis of colloidal semiconductor nanocrystals: (1) the rational design of the synthesis protocol aiming at the optimization of the reaction parameters in a minimum number of experiments; (2) the transfer of the procedure to the gram scale, while maintaining a low size distribution and maximizing the reaction yield. Concerning the first point, the design-of-experiment (DOE) method has been applied to the synthesis of colloidal CdSe nanocrystals. We demonstrate that 16 experiments, analyzed by means of a Taguchi L16 table, are sufficient to optimize the reaction parameters for controlling the mean size of the nanocrystals in a large range while keeping the size distribution narrow (5-10%). The DOE method strongly reduces the number of experiments necessary for the optimization as compared to trial-and-error approaches. Furthermore, the Taguchi table analysis reveals the degree of influence of each reaction parameter investigated (e.g., the nature and concentration of reagents, the solvent, the reaction temperature) and indicates the interactions between them. On the basis of these results, the synthesis has been scaled up by a factor of 20. Using a 2-L batch reactor combined with a high-throughput peristaltic pump, different-sized samples of CdSe nanocrystals with yields of 2-3 g per synthesis have been produced without sacrificing the narrow size distribution. In a similar setup, the gram-scale synthesis of CdSe/CdS/ZnS core/shell/shell nanocrystals exhibiting a fluorescence quantum yield of 81% and excellent resistance of the photoluminescence in presence of a fluorescent quencher (aromatic thiol) has been achieved.PACS: 81.20.Ka, 81.07.Bc, 78.67.Bf
The precursor (AgIn)x Zn2(1–x)(S2CN(C2H5)2)4 was used to prepared AgInS2–ZnS nanocrystals with different compositions (x = 0.4 and x = 0.7) and with different time of reaction (10 min and 75 min). The photoluminescence features of the nanocrystals were addressed by combining steady‐state spectroscopy and light‐induced electron paramagnetic resonance. Both techniques showed the contribution of at least two components for the emission, previously assigned to surface and intrinsic states. Light‐induced electron paramagnetic resonance allowed detection of the photocreation both of irreversible paramagnetic species that are likely responsible for the nano‐crystals degradation assigned to surface states and of reversible paramagnetic species assigned to intrinsic states. Moreover, reversible bistable paramagnetic states were observed. This Letter provides a scheme that might be useful in addressing the well‐known problem of aging of the nanocrystals. (© 2014 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.