Precipitation hardenable (PH) nickel (Ni) alloys are often the most reliable engineering materials for demanding oilfield upstream and subsea applications especially in deep sour wells. Despite their superior corrosion resistance and mechanical properties over a broad range of temperatures, the applicability of PH Ni alloys has been questioned due to their susceptibility to hydrogen embrittlement (HE), as confirmed in documented failures of components in upstream applications. While extensive work has been done in recent years to develop testing methodologies for benchmarking PH Ni alloys in terms of their HE susceptibility, limited scientific research has been conducted to achieve improved foundational knowledge about the role of microstructural particularities in these alloys on their mechanical behaviour in environments promoting hydrogen uptake. Precipitates such as the ','' and δ-phase are well known for defining the mechanical and chemical properties of these alloys. To elucidate the effect of precipitates in the microstructure of the oil-patch PH Ni alloy 718 on its HE susceptibility, slow strain rate tests under continuous hydrogen charging were conducted on material after several different age-hardening treatments. By correlating the obtained results with those from the microstructural and fractographic characterization, it was concluded that HE susceptibility of oil-patch alloy 718 is strongly influenced by the amount and size of precipitates such as the ' and'' as well as the δ-phase rather than by the strength level only. In addition, several HE mechanisms including hydrogen-enhanced decohesion and hydrogen-enhanced local plasticity were observed taking place on oil-patch alloy 718, depending upon the characteristics of these phases when present in the microstructure.This article is part of the themed issue 'The challenges of hydrogen and metals'.
Low-alloyed, high-strength steels with yield strength above 1200 MPa are frequently used in the automotive industry, in order to reduce the weight of the components. However, hydrogen embrittlement susceptibility is often a concern for this group of materials. Hydrogen can be produced on the metal surface, as a result of electrochemical corrosion reaction during service. The aim of this study is to evaluate the impact of the various loading procedures according to the existing technical specifications for environmental hydrogen embrittlement (EHE) testing. The hydrogen embrittlement susceptibility of high strength fasteners (strength class 14.8) was tested according to the well-established testing specifications: DIN 50969-2, DIN EN ISO 7539, ASTM F1624-12 in 5 wt.-% sodium chloride solution acidified to pH 3 with hydrochloric acid. Open circuit potential measurements were carried out during the testing procedure to gain understanding of the damage process in each of the testing approaches. Under the chosen testing conditions, rising step load (RSL) testing approach, specified in ASTM F1624-12, appeared as the most sensitive method for the evaluation of the material's hydrogen embrittlement susceptibility.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.