The goal of the present paper was to synthesize, characterize, and evaluate the performance of the modified composite based on magnetite (Fe3O4) and polyvinyl alcohol (PVA). The obtained composite was used to degrade Methyl Orange dye from synthetic wastewater by a laboratory photocatalytic reactor. Various parameters of the photodegradation process were tested: composite dosage, amount of hydrogen peroxide (H2O2), and pH. The composite was characterized by Fourier Transform Infrared (FTIR) Spectroscopy, X-ray Diffraction (XRD), and Scanning Electron Microscopy (SEM). The degradation experiments indicated that the complete dye decolorization depended on the amount of H2O2. In addition, the H2O2 could accelerate Methyl Orange degradation to more highly oxidized intermediates in the presence of UV light (99.35%). The results suggested that the obtained modified composite could be used to treat wastewater containing various types of dyes.
The main goal of the present paper was to synthesize the polyvinyl alcohol-SiO2 nanoparticles polymeric membrane by wet-phase inversion method. The efficiency of prepared membranes (without and with SiO2) was investigated using a versatile laboratory electrodialysis system filled with simulated wastewaters that contain zinc ions. All experiments were performed at following conditions: the applied voltage at electrodes of 5, 10 and 15 V, a concentration of zinc ions solution of 2 g L−1, time for each test of 1 h and at room temperature. The demineralization rate, extraction percentage of zinc ions, current efficiency and energy consumption were determined. The polymeric membranes were characterized by Fourier Transforms Infrared Spectroscopy-Attenuated Total Reflection (FTIR-ATR), Scanning Electron Microscopy (SEM) and Electrochemical Impedance Spectroscopy (EIS). The higher value of percentage removal of zinc ions (over 65%) was obtained for the polymeric membrane with SiO2 nanoparticles, at 15 V. The FTIR-ATR spectra show a characteristic peak located at ~1078 cm−1 assigned to the Si-O-Si asymmetrical stretching. SEM images of the polymeric membrane with SiO2 nanoparticles show that the nanoparticles and polymer matrix were well compatible. The impedance results indicated that the SiO2 nanoparticles induced the higher proton conductivity. The final polymeric membranes can be used for the removal of various metallic ions, dyes, organic or inorganic colloids, bacteria or other microorganisms from different natural waters and wastewaters.
Magnesium–aluminum (Mg-Al) and magnesium–aluminum–nickel (Mg-Al-Ni) layered double hydroxides (LDHs) were synthesized by the co-precipitation method. The adsorption process of Mn2+ from synthetic wastewater was investigated. Formation of the layered double hydroxides and adsorption of Mn2+ on both Mg-Al and Mg-Ni-Al LDHs were observed by X-ray diffraction (XRD), Scanning Electron Microscopy (SEM) and Energy Dispersive Spectrometry (EDX) analysis. XRD patterns for prepared LDHs presented sharp and symmetrical peaks. SEM studies revealed that Mg-Al LDH and Mg-Al-Ni LDH exhibit a non-porous structure. EDX analysis showed that the prepared LDHs present uniformly spread elements. The adsorption equilibrium on these LDHs was investigated at different experimental conditions such as: Shaking time, initial Mn2+ concentration, and temperatures (10 and 20 °C). The parameters were controlled and optimized to remove the Mn2+ from synthetic wastewater. Adsorption isotherms of Mn2+ were fitted by Langmuir and Freundlich models. The obtained results indicated that the isotherm data fitted better into the Freundlich model than the Langmuir model. Adsorption capacity of Mn2+ gradually increased with temperature. The Langmuir constant (KL) value of Mg-Al LDH (0.9529 ± 0.007 L/mg) was higher than Mg-Al-Ni LDH (0.1819 ± 0.004 L/mg), at 20 °C. The final adsorption capacity was higher for Mg-Al LDH (91.85 ± 0.087%) in comparison with Mg-Al-Ni LDH (35.97 ± 0.093%), at 20 °C. It was found that the adsorption kinetics is best described by the pseudo-second-order model. The results indicated that LDHs can be considered as a potential material for adsorption of other metallic ions from wastewater.
A novel hydrogel composite based on gellan gum and graphene oxide (GG/GO) was synthesized, characterized and tested for sorption capacity in this work. The microstructural, thermogravimetric and spectroscopic analysis confirmed the formation of the GG/GO composite. Comparative batch sorption experiments revealed a sorption capacity of the GG/GO composite for Zn (II) ions of approximately 2.3 higher than that of pure GG. The GG/GO composite exhibits a maximum sorption capacity of 272.57 mg/g at a pH of Zn (II) initial solution of 6. Generally, the sorption capacity of the sorbents is approximately 1.5 higher in slightly acidic conditions (pH 6) comparative with that for strong acidic conditions (pH 3). The sorption isotherms revealed that the sorption followed a monolayer/homogenous behavior. The sorption kinetic data were well fitted by the pseudo-second-order kinetic model, and were consistent with those derived from sorption isotherms. The intraparticle diffusion was considered to be the rate-determining step. Two main sorption mechanisms for Zn (II) were identified namely, ion exchange at low pH values, and both ion exchange and chemisorption in weekly acidic conditions.
The capacity of ion exchange resins, MN 500 and C100 H, for the removal of copper ions from aqueous solution has been investigated under different conditions, namely: initial solution pH, initial metal-ion concentration and contact time. The adsorption of Cu(II) on these resins follows the first-order reversible kinetic. The film diffusion of Cu (II) in these ion exchange resins was shown to be the main rate limiting step. The studies showed that these cation exchange resins can be used as efficient adsorbent material for the removal of Cu (II) from aqueous solutions. The adsorption process, which is pH dependent, shows maximum removal of copper in the pH range 2-7 for an initial copper concentration of 10 mg/L. The adsorption rate constants for all these kinetic models have been calculated. Results showed that the intraparticle diffusion and initial Cu(II) sorption into resins was the main rate limiting step. The uptake of copper by the ion exchange resins is reversible and thus has good potential for the removal/recovery of copper from aqueous solutions. After the experiments we concluded that such ion exchange resins can be used for the efficient removal of copper from water and wastewater.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.