Chemical esterification of wood biopolymers using acetic acid is a green method to sustain and improve the physical properties of native tropical hardwoods in part by drastically reducing the surface energy.
Bamboo culms of Bambusa vulgaris Schrad. were collected from two locations in moist forests and two sites in derived Savanna zones in South West Nigeria. The study involved chemical analyses, density variability, bonding tests, gluability tests, and measurements of bending strength of the bamboo in addition to durability testing with decay fungi and treatability of glued boards with a copper-based wood preservative. Chemical analyses showed a uniform composition of the bamboo with a cellulose content of 45 to 47.5% and a lignin content of 23 to 25.6% as the predominant chemical constituents. An average wood density of 700 kg/m 3 was a prerequisite for high mechanical strength. The moduli of elasticity were high and exceeded 14 kN/mm 2 for bamboo boards and 13 kN/mm 2 for finger joints. Bamboo boards from all growth sites showed high moduli of rupture in the range of 150 to 166 N/mm 2 and 72.9 to 94.7 N/mm 2 for boards and finger joints, respectively. Bamboo from the four sites showed variable mass loss with the EN-113 (1996) test method, which classifies this biomass as a moderately to non-durable plant material. White rot fungus (Trametes versicolor) caused the highest mass losses (11.2 to 16.8%). The bamboo showed good treatability using a 500-kg/m 3 solution of a copper-based preservative.
This study was aimed at determining the optimal glue quantity for bamboo lamination. Bamboo laminated boards were produced using glue applied at three different rates: 150 g/m 2 , 200 g/m 2 and 250 g/m 2. The boards produced were evaluated for their physical (density, longitudinal, tangential, radial and volumetric shrinkage) and mechanical (impact bending strength, modulus of elasticity, modulus of rupture and maximum compressive strength parallel to grain properties. It was discovered that the boards were uniform in their investigated physical properties but the glue quantity significantly influenced both the impact bending strength and modulus of rupture of the boards. Based on the results, it was observed that the boards produced with glue applied at the rate of 200 g/m 2 met all the technical specifications on the basis of the investigated physical and mechanical properties, hence, concluded to be the optimal glue quantity for bamboo lamination.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.