In uniform hot working tests, the flow curves strain harden to a steady state plateau that depends on temperature and strain rate. The underlying mechanism is dynamic recovery which rises with strain to balance the work hardening, resulting in subgrains that are larger and more perfect as T rises and E falls. Subgrains are observed in the extrudate following the pattern established in hot workability tests. Moreover, their formation in the upset billet and throughout the deformation zone has been examined as a means to delineate its thermal and mechanical development. Substructure in the extrudate substantially improves its mechanical properties. With increasing Mg solute, substructure recovery is reduced so that the strength and the tendency for recrystallization are increased. Moreover, in alloys above 5% Mg, most notably containing large Mn-rich constituent particles, dynamic recrystallization nuclei form in the most intensely strained regions of the deformation zone and also speed up static recrystallization in the extrudate.Resume-Lors d'essai de formage a chaud uniforme, les courbes d'ecoulement se durcissent par ecrouissage jusqu'a un plateau constant qui depend de la temperature et du taux de deformation. Le mecanisme sousjacent est la restauration dynamique qui augmente avec la deformation pour balancer Ie durcissement par ecrouissage, resultant en sous-grains qui sont plus gros et plus parfaits a mesure que la T s'eleve et que f s'abaisse. On observe des sous-grains dans la forme d'extrusion, suivant Ie modele etabli lors d'essais de formage a chaud. De plus, on a examine leur formation dans la billette refoulee et dans toute la zone de deformation, comme un moyen de delimiter leur developpement thermique et mecanique. La sous-structure dans la forme d'extrusion ameliore substantiellement ses proprietes mecaniques. Avec une augmentaion du solute de Mg, la restauration de la sous-structure est reduite de telle sorte que la resistance et la tendance ala recristallisation sont augmentees. De plus, dans les alliages de plus de 5% Mg, contenant visiblement de grosses particules constituantes riches en Mn, des noyaux de recristallisation dynamique se forment dans les regions les plus intensement deformees de la zone de deformation et aussi augmentent la vitesse de recrisallisation statique de la forme d'extrusion.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.