Ti-6Al-4V alloy has been widely used in restorative surgery due to its high corrosion resistance and biocompatibility. Nevertheless, some studies showed that V and Al release in the organism might induce cytotoxic effects and neurological disorders, which led to the development of V-free alloys and both V-and Al-free alloys containing Nb, Zr, Ta, or Mo. Among these alloys, Ti-13Nb-13Zr alloy is promising due to its better biomechanical compatibility than Ti-6Al-4V. In this work, the corrosion behavior of Ti, Ti-6Al-4V, and Ti-xNb-13Zr alloys (x ¼ 5, 13, and 20) was evaluated in Ringer's solution (pH 7.5) at 37 8C through open-circuit potential measurements, potentiodynamic polarization, and electrochemical impedance spectroscopy. Spontaneous passivity was observed for all materials in this medium. Low corrosion current densities (in the order of 10 À7 A/cm 2 ) and high impedance values (in the order of 10 5 Vcm 2 at low frequencies) indicated their high corrosion resistance. EIS results showed that the passivating films were constituted of an outer porous layer (very low resistance) and an inner compact layer (high resistance), the latter providing the corrosion resistance of the materials. There was evidence that the Ti-xNb-13Zr alloys were more corrosion resistant than both Ti and Ti-6Al-4V in Ringer's solution.

Ti-Nb-Zr alloys are interesting materials for implant applications due to the atoxic character of the Nb and Zr alloying elements and to their low elastic modulus when compared to CP-Ti. In this work, the corrosion behaviour of CP-Ti, Ti-5Nb-13Zr, Ti-13Nb-13Zr, and Ti-20Nb-13Zr alloys was investigated in Ringer’s solution of pH 2, 5, and 7.5 without fluorides and containing 1000 ppm F at 37°C, through open-circuit potential measurements, potentiodynamic polarization, and electrochemical impedance spectroscopy. The four materials showed a passive behavior in Ringer's solution without fluorides for pH ranging from 2 to 7.5 and in Ringer's solution of pH 5 and 7.5 containing 1000 ppm F but presented an active behavior in Ringer's solution of pH 2 containing fluorides. The corrosion resistance of all materials in Ringer's solution decreases with both decrease of pH and addition of fluorides. Ti-13Nb-13Zr alloy is a little more corrosion resistant than the Ti-5Nb-13Zr and Ti-20Nb-13Zr alloys and, in most conditions, the Ti-Nb-Zr alloys present higher corrosion resistance than CP-Ti.