In this study, heavy-metal-free orange light-emitting ZnSe:Mn2+/ZnS doped-core/shell (d-C/S) quantum dots (QDs) were synthesized using a nucleation doping strategy. To synthesize high quality d-C/S QDs with high photoluminescence (PL) quantum yield (QY), the Mn2+ concentration was optimized. The resulting ZnSe:Mn2+(5%)/ZnS d-C/S QDs showed a high PL QY of 83.3%. The optical properties of the synthesized QDs were characterized by absorption and PL spectroscopy. Their structural and compositional properties were studied by X-ray diffraction, transmission electron microscopy, and energy dispersive X-ray spectroscopy. After doping Mn2+ into a ZnSe core, the ZnSe:Mn2+/ZnS d-C/S QDs showed a large Stokes shift of 170 nm. The ZnSe:Mn2+/ZnS d-C/S QDs were embedded in a poly(lauryl methacrylate) (PLMA) polymer matrix and the ZnSe:Mn2+/ZnS-based polymer film was fabricated. The fabricated ZnSe:Mn2+/ZnS-PLMA film was highly transparent in the visible spectral region (transmittance > 83.8% for λ ≥ 450 nm) and it exhibited bright orange light under air mass (AM) 1.5G illumination using a solar simulator. The optical path-dependent PL measurement of the ZnSe:Mn2+/ZnS-PLMA film showed no PL band shift and minimal PL decrease under variation of excitation position. These results indicate that the highly efficient and large Stokes shift-emitting ZnSe:Mn2+/ZnS QDs are promising for application to luminescent solar concentrators.
The synthesis of silver nanoparticles loaded on the activated carbon (AC) surface were performed under SCW condition at 673 K and 31.15 MPa in a batch reactor. In supercritical region, fine particles are rapidly synthesized due to reaction rate increase at low dielectric constant of supercritical water. Samples were prepared with different concentrations of silver acetate solution and various reaction times. The synthesized silver loaded on AC particles were characterized by the Fourier transform infrared spectroscopy (FTIR),X-ray diffraction (XRD), Scanning electron microscopy (SEM) and Transmission electron microscopy (TEM). FTIR spectrum of primary activated carbon, activated carbon treated under supercritical water condition and synthesized AC-Ag was compared. The particles size and crystallite size of silver deposited on AC surface were analyzed by TEM and XRD, respectively.
Blue-light-emitting ZnSe core (C) and ZnSe/ZnS core/shell (C/S) quantum dots (QDs) were synthesized with phosphine-free precursors by a thermal decomposition method in paraffin oil solvent and applied to QD-converted light-emitting diodes (LEDs). The optical properties of the synthesized ZnSe C and ZnSe/ZnS C/S QDs were characterized by absorption spectroscopy and photoluminescence spectroscopy. Additionally, the quantum efficiency of the QDs was investigated. Their structural properties were studied with X-ray crystallography and transmission electron microscopy. The ZnSe/ZnS C/S QDs showed deep-blue light peaking at 425 nm. The blue-light-emitting ZnSe/ZnS C/S QDs were used as color-converting materials for near-ultraviolet LED-pumped blue LEDs and combined with yellow-light-emitting Zn-Cu-In-S/ZnS C/S QDs to fabricate white LEDs. The white LEDs showed warm white light [(CIE x, CIE y) = (0.4088, 0.3987)], Tc = 3488 K, and Ra = 61.2]. The results indicate that the ZnSe/ZnS C/S QDs have good potential for white light application after further improvements to their optical properties.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.