Deep beams are more susceptible to shear failure, and therefore reparation is a crucial for structural reinforcements. Shear failure is structural concrete failure in nature. It generally occurs without warning; however, it is acceptable for the beam to fail in bending but not in shear. The experimental study presented the structural behavior of the deep beams of reinforced concrete (RC) that reinforces the web openings with externally connected carbon fiber reinforced polymer (CFRP) composite in the shear zone. The structural behavior includes a failure mode, and cracking pattern, load deflection responses, stress concentration and the reinforcement factor were investigated. A total of nine reinforced concrete deep beams with openings strengthened with CFRP and one control beam without an opening have been cast and tested under static four-point bending load till failure. The experimental results showed that the increase the size of the opening causes an increase in the shear strength reduction by up to 30%. Therefore, the larger the openings, the lower the capability of load carriage, in addition to an increase in the number of CFRP layers that could enhance the load carrying capacity. Consequently, utilization of the CFRP layer wrapping technique strengthened the shear behavior of the reinforced concrete deep beams from about 10% to 40%. It was concluded that the most effective number of CFRP layers for the deep beam with opening sizes of 150 mm and 200 mm were two layers and three layers, respectively.
Producing high-strength self-compacting concrete (SCC) requires a low water-cement ratio (W/C). Hence, using a superplasticizer is necessary to attain the desired self-compacting properties at a fresh state. The use of low W/C results in very brittle concrete with a low deformation capacity. This research aims to investigate the influence of crumb rubber (CR), fly ash (FA), and nanosilica (NS) on SCC’s workability and mechanical properties. Using response surface methodology (RSM), 20 mixes were developed containing different levels and proportions of FA (10–40% replacement of cement), CR (5–15% replacement of fine aggregate), and NS (0–4% addition) as the input variables. The workability was assessed through the slump flow, T500, L-box, and V-funnel tests following the guidelines of EFNARC 2005. The compressive, flexural, and tensile strengths were determined at 28 days and considered as the responses for the response surface methodology (RSM) analyses. The results revealed that the workability properties were increased with an increase in FA but decreased with CR replacement and the addition of NS. The pore-refining effect and pozzolanic reactivity of the FA and NS increased the strengths of the composite. Conversely, the strength is negatively affected by an increase in CR, however ductility and deformation capacity were significantly enhanced. Response surface models of the mechanical strengths were developed and validated using ANOVA and have high R2 values of 86–99%. The optimization result produced 36.38%, 4.08%, and 1.0% for the optimum FA, CR, and NS replacement levels at a desirability value of 60%.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.