No abstract

No abstract

Nowadays, zinc oxide (ZnO) has attracted attention in research and development because of its remarkable antibacterial properties. Chitosan/ZnO nanoparticles were successfully synthesized via microwave heating. The objectives of this work were to investigate the effect of stabilizer, power heating and time heating on size of chitosan/ZnO nanoparticles and to determine antibacterial activity against pathogenic bacteria, where chitosan was used as a stabilizing agent. Chitosan/ZnO nanoparticles were analyzed by Fourier Transform Infra Red (FTIR), X-ray Diffraction (XRD), Field Emission Scanning Electron Microscopy (FESEM), and Zetasizer instrument. The power heating and time heating were varied from 400 to 800 Watt and 4 to 8 minutes, respectively. The presence of chitosan has role on preventing the nanoparticles from agglomeration by producing a milky solution of chitosan/ZnO nanoparticles without any suspensions. The increase of power and time heating improved the size of nanoparticles. The peak in FTIR spectrum at around 427 cm -1 was confirmed the existence of the ZnO phase. XRD patterns showed that the chitosan/ZnO nanoparticles materials were pure phase with average crystalline size is 130 nm. FESEM revealed that chitosan/ZnO nanoparticles were uniformly distributed with the mean value of size is 70 nm and spherical shaped. Further impact of power and time heating on the size of the chitosan/ZnO nanoparticles can be shown by a nanoparticles size distribution with the average of 30 to 90 nm. The results showed that chitosan/ZnO nanoparticles have displayed an antibacterial inhibition zone against Gram-positive S. aureus and Gram-negative E. coli which 16.0 and 13.3 mm, respectively. Chitosan/ZnO nanoparticles were synthesized in this work presented have potential application to prevent bacterial infections.

The conventional heating methods of nanoparticle synthesis regularly depend on the energy inputs from outer heat sources that resulted high energy intake and low reaction competences. In this paper ZnO nanoparticles stabilized with gum arabic are synthesized using precipitating method assisted by simple and cost effective microwave heating technique. The objective of this work is to investigate the effect of microwave irradiation time towards ZnO nanoparticles morphology and size. The effect of microwave irradiation time has been investigated at 2, 4, 6, and 10 minutes. Dynamic Light Scattering (DLS) was employed to measure the size of ZnO nanoparticles. Ultraviolet–Visible spectroscopy (UV-vis), Fourier-Transform Infrared Spectroscopy (FTIR) and X-Ray Diffraction (XRD) were used for the characterization of the ZnO nanoparticles. UV-vis absorption spectrum was found in the range of 350 nm indicating the absorption peak of ZnO nanoparticles. FTIR spectra showed peaks range from 424 to 475 cm–1 which indicating standard of Zn–O stretching. The presence of (100), (002), and (101) planes were apparent in the XRD result, indicating the crystalline phase of ZnO nanoparticles. The increase in the microwave irradiation time affected the processes of nucleation and crystal growth promoted larger ZnO nanoparticles size. Microwave irradiation time at 2 minutes was selected as the best microwave irradiation time for smallest ZnO nanoparticles averaging about 168 nm sizes based on DLS analysis. Copyright © 2019 BCREC Group. All rights reservedReceived: 1st October 2018; Revised: 22nd November 2018; Accepted: 12nd December 2018; Available online: 25th January 2019; Published regularly: April 2019How to Cite: Pauzi, N., Zain, N.M., Yusof, N.A.A. (2019). Microwave-assisted Synthesis of ZnO Nanoparticles Stabilized with Gum Arabic: Effect of Microwave Irradiation Time on ZnO Nanoparticles Size and Morphology. Bulletin of Chemical Reaction Engineering & Catalysis, 14 (1): 182-188 (doi:10.9767/bcrec.14.1.3320.182-188)Permalink/DOI: https://doi.org/10.9767/bcrec.14.1.3320.182-188

No abstract

Apart from biocompatibility, hydrogel films with good physical, morphology, swelling, and antibacterial properties are required for biomedical applications. In this study, the effects of nanofiller (i.e., zinc oxide (ZnO) nanoparticles) on physical, morphology, swelling, and antibacterial properties of hydrogel film were investigated. The new chitosan/gelatin/ZnO hydrogel films were synthesized using solution casting method by blending the chitosan and gelatin solutions with ZnO nanoparticles. The use of glycerol (plasticizing agent) could enhance the durability and flexibility of the hydrogel film. From the FTIR results, it was found that chemical reactions occurred of gelatin was between 1500 cm-1 to 800 cm-1. On the other hand, the SEM results showed that the pore size distribution within the hydrogel film varied from 20µm to 700µm. The antibacterial properties ZnO hydrogel film against bacteria such as Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli) were evaluated using the zone of inhibition method. The antibacterial activity (against the S. aureus bacteria) of the new ZnO hydrogel film was more promising than that of the nanoparticle-free hydrogel film. The current findings showed that the new chitosan/gelatin/ZnO hydrogel film could be used in biomedical application.