Uniaxial tensile and bending properties of lightweight thermally bonded nonwoven layers produced from the blends of Estabragh (milkweed)/polypropylene fibers have been focused in this paper. For this, different material variables such as the blend ratio as well as some parameters of thermal bonding process including the calendering speed and temperature were considered in this study. Eighteen fibrous samples from six Estabragh/polypropylene blend ratios of 10/90, 25/75, 40/60, 55/45, 70/30, and 85/15 at three different layer weights (g/m 2 ) were produced on a laboratory-scale carding machine. During needle-punching operation, different punch densities at low levels of 20, 30, and 40 punches/cm 2 were applied to the samples in order to increase the layer strength by increasing the fiber entanglement while the fiber breakage remains in such minimized level. Thermal bonding process was then carried out on the produced nonwoven samples using an apparatus equipped with a pair of heated calendering in which three different levels of temperatures as well as three levels of calendering speed were considered as the process variables. Taguchi's analyzing method was employed for statistical investigations of the results. The findings showed that the blend ratio of fibers, layer weight, and the applied temperature during the thermal bonding process
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.