The foaming of aluminum melt of LKR‐Austria is investigated. The foaming was performed in a furnace chamber at adiabatic conditions to keep the foam in liquid state. The foams were taken out from the chamber after 1, 10 and 100 min isothermal holding time and cooled in air or quenched in water. The final cellular structure depends on the following parameters: particle (composition, shape and size, volume fraction), gas (composition and purity), the particle‐surface interactions, matrix alloy composition and temperature of foaming.Metallographical examinations are carried out after freezing the foamed melt by the help of Scanning Electron Microscopy. The cell wall thickness, the particle distribution and the existing phases are determined. Transmission Electron Microscopy and Auger Electron Spectroscopy are used to analyze the surface skin of the cells and to determine the oxide layer thickness depending on the different foaming gases.An equipment called High Temperature Maximum Bubble Pressure Tensiometer (HTMBPT) was built to measure the apparent surface tension of the particle‐stabilized melt. Semi quantitative description of the experimental phenomena are presented.

No abstract

Articles you may be interested inFilm thickness mediated transition in the kinetics of electric current induced flow of thin liquid metal films Appl. Phys. Lett. 104, 214102 (2014); 10.1063/1.4880208In situ X-ray reflectivity of indium supplied on GaN templates by metal organic vapor phase epitaxy Strength of metals in liquid and solid states at extremely high tension produced by femtosecond laser heating AIP Conf.

No abstract