The aim of this study was to evaluate the effect of remaining dentin thickness (RDT) on resin composite bond strength to dentin surfaces when using various adhesive systems. One of three adhesives, Clearfil SE Bond, Single Bond or Clearfil Tri-S Bond, followed by Z100 resin composite were built up on flat dentin surfaces of human molars. The teeth were sectioned obtaining beams with crosssectional areas of approximately 1 mm 2 . RDT was measured and microtensile bond strength was determined. Resulting data were categorized into four groups: RDT<2 mm; 2≤RDT<3 mm; 3≤RDT<4 mm; RDT≥4 mm. Clearfil SE Bond showed a correlation between µTBS and RDT. Single Bond showed no significant difference in µTBS for any RDT. The bond strength of resin composite to the different RDT flat dentin surfaces was affected by the adhesive system used.
This study evaluated the effect of two adhesive systems and four resin-based composites on the marginal sealing and cavity wall adaptation of restorations with different C-factors. Cylindrical cavities, 1 mm deep and 3 mm in diameter (C-factor=2.3)or 2 mm in diameter(C-factor=3) , were prepared on superficial bovine dentin surfaces. The teeth were restored with Clearfil SE Bond or Single Bond adhesive system followed by hybrid (Photo Clearfil Bright or Z100) or flowable (Filtek Flow or Estelite LV)resin composite. After thermocycling, a dye penetration test was carried out to evaluate the degree of marginal leakage and cavity-wall gap formation. Cavity-wall gap formation increased when the C-factor increased from 2.3 to 3, except for Estelite LV resin composite. In terms of marginal sealing, Clearfil SE Bond showed better performance than Single Bond. When using Clearfil SE Bond, flowable composites improved resin composite adaptation to the cavity wall compared with hybrid composites.
This study evaluated the effect of thermal stress on marginal sealing and cavity wall adaptation using two adhesive systems. Cylindrical cavities were prepared in superficial dentin of bovine incisors and bonded with Clearfil SE Bond or Single Bond adhesive. Cavities were bulk-filled with Photo Clearfil Bright or Filtek Flow resin composite and light-cured for 40 seconds. Specimens were thermocycled for 0, 500, or 5000 times. A dye penetration test was carried out to determine adaptation to the cavity wall. Dye penetration length was calculated as a percentage of the total cavity wall length. Clearfil SE Bond showed excellent marginal sealing and cavity wall adaptation regardless of composite type up to 500 cycles of thermal stress. As for the Single Bond groups, significantly greater marginal leakage occurred after 500 cycles. At 5000 cycles of thermal stress, both adhesive systems showed significantly decreased marginal integrity compared with the 0 cycle group.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.