Iron oxide, in the form of magnetite (MG)-functionalized porous wollastonite (WL), was used as an adsorbent for heavy metal ions (cadmium and nickel) and oxyanions (chromate and phosphate) removal from water. The porous WL was synthesized from calcium carbonate and siloxane by controlled sintering process using low molecular weight submicrosized poly(methyl methacrylate) as a pore-forming agent. The precipitation of MG nanoparticles was carried out directly by a polyol-medium solvothermal method or via branched amino/carboxylic acid cross-linker by solvent/nonsolvent method producing WL/MG and WL-γ-APS/MG adsorbents, respectively. The structure/properties of MG functionalized WL was confirmed by applying FTIR, Raman, XRD, Mössbauer, and SEM analysis. Higher adsorption capacities of 73.126, 66.144, 64.168, and 63.456 mg g −1 for WL-γ-APS/MG in relation to WL/MG of 55.450, 52.019, 48.132, and 47.382 mg g −1 for Cd 2+ , Ni 2+ , phosphate, and chromate, respectively, were obtained using nonlinear Langmuir model fitting. Adsorption phenomena were analyzed using monolayer statistical physics model for single adsorption with one energy. Kinetic study showed exceptionally higher pseudosecond-order rate constants for WL-γ-APS/MG, e.g., 1.17-13.4 times, with respect to WL/MG indicating importance of both WL surface modification and controllable precipitation of MG on WL-γ-APS.

Due to its outstanding electrical characteristics, such as the low temperature expansion coefficient, low dielectric constant and good mechanical properties, cordierite, 2MgO⋅2Al 2 O 3 ⋅ 5SiO 2 , is a very attractive high-temperature ceramic material. In order to accelerate the process of sintering, 2.50 mass% Bi 2 O 3 has been added to the starting mixtures. Liquid phase sintering caused by the presence of bismuth-oxide lowers the temperature of cordierite formation. The mechanical activation of the starting mixtures (0-56 min in vibro-mill) additionally lowers sintering temperatures. The sintering process was performed at 1200, 1300, 1350 and 1400°C, for 2 h. The particle size analysis (PSA) was employed in order to determine the changes in the particle size of the mechanically treated powders. The phase composition of the starting powders and sintered materials was analyzed by the X-ray diffraction method. Furthermore, scanning electron microscopy (SEM) was used in the analysis of the powder morphology.

No abstract

Corundum (α-alumina) is a suiTab. material for usage in various industry fields owing to its chemical stability, electrical and mechanical features. It is known that properties of ceramics could be modified by addition of different oxides, as well as by changing the consolidation parameters. In this respect, alumina was doped with 1 wt.% of Cr 2 O 3 , Mn 2 O 3 and NiO, followed by 1 hour of mechanical activation in a high-energy planetary ball mill. A sensitive dilatometer was used for sintering of powder mixtures up to 1400 o C and recording the obtained dilatation. The final density varied between cca. 1.9 and 3.3 g/cm 3. Microstructural changes were detected by SEM measurements. Changes in electrical permittivity and loss tangent were associated with the preparation conditions (types of additives, duration of mechanical activation). For a given mixture, the sintering increases the relative permittivity and decreases losses, exhibiting the optimal values of 8.32 and 0.027, respectively, for the sample activated 60 minutes and sintered, with the addition of MnO 2. Mechanical measurements indicate significant differences in strength with the addition of different transition metal oxides. Samples with Mn and Ni, activated and sintered, with strength of 121 and 86 MPa, respectively, have a significantly higher tensile strength than the other tested samples, due to their more compact microstructures.

Cordierite-based ceramic materials are attracting much interest for their various applications in industry, for manufacturing multilayer circuit boards, catalytic converters, filters, thermal insulation, kiln furniture, components of portable electronic devices, etc. In order to reduce production costs and modify cordierite-based materials, mechanical activation can be used. In this study, microstructural and electrical properties of mechanically activated MgO-Al 2 O 3 -SiO 2 system have been analyzed. The mixtures of MgO-Al 2 O 3 -SiO 2 powders were mechanically activated in a planetary ball mill for the time periods from 0 to 160 min. Morphological investigations have been performed on the obtained powders. The effects of activation and two-step sintering process on microstructure were investigated by scanning electron microscopy (SEM). Electrical measurements showed variations of the dielectric constant (ε r ) and loss tangent (tan δ) as a function of time of mechanical treatment.