Zinc alloy (ZA27) syntactic foams (SF) were manufactured using expanded perlite (EP) particles and counter-gravity infiltration casting. Due to a variation of the metallic matrix content, the density of the produced foam samples varied from 1.78 to 2.03 g·cm−3. As-cast and solution heat-treated samples were tested to investigate the compressive properties of the ZA27 syntactic foam. To this end, quasi-static compression tests were conducted. In addition, microstructural analysis of the as-cast and heat-treated syntactic foams was carried out using scanning electron microscopy. The results indicate that the heat treatment alters the microstructure of the ZA27 alloy matrix from a multiphase dendrite to a spheroidized microstructure with improved ductility. Moreover, the heat treatment considerably enhances the energy absorption and plateau stress ( σ pl ) of the syntactic foam. Optical analysis of the syntactic foams under compression shows that the dominant deformation mechanism of the as-cast foams is brittle fracture. In comparison, the heat-treated samples undergo a more ductile deformation.

No abstract

This paper introduces a novel functionally graded metallic syntactic foam. The investigated foams are manufactured while using infiltration casting where molten A356 aluminum flows into the interstitial voids of packed expanded perlite (EP) particle beds. The partial pre-compaction of particle beds enables the creation of distinct and reproducible density gradients within the syntactic foam. In this study, the samples are produced using four gradually increasing compaction forces and are compared to non-compacted samples. X-ray imaging is used to detect the resulting spatial variation of foam density. In addition, quasi-static compression tests are performed to determine the mechanical foam properties. The results suggest that particle pre-compaction is an efficient tool for tailoring the density and mechanical properties of these novel functionally graded materials.

No abstract