In this work, comparison of TiO2 additions on the physical properties of YBa2Cu3Oδ superconductor system with nominal starting compositions at x= 0, 1, 2, and 5 wt.% was studied derived via solid state reaction and co-precipitation method. The samples were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The result from XRD shown that all the samples were polycrystalline for solid state reaction, while single phase appear for co-precipitation methods. The intensity of the peak become higher with increasing amount of TiO2 addition indicating the presence of increased amount of the unreacted in the samples. The refine lattice parameters indicated that all the samples have an orthorhombic crystal structure without occurrence of orthorhombic-tetragonal phase transformation. Furthermore, from SEM images for solid state reaction and co-precipitation method showed that the grain size of the samples decreased with TiO2 increased. Small addition of TiO2 derived from co-precipitation method enhanced the YBCO microstructures.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.