This study examined the effectiveness of zeolite addition to reduce the autogenous shrinkage of high-performance cement-based concrete (HPC). The zeolites were replaced up to 15% of the cement content by weight and their mean particle size varied from 5.6 to 16.7 µm. To evaluate the crack resistance of HPC containing zeolites, the ring tests and internal relative humidity measurements were performed at different ages. The compressive strengths were determined at 3, 7, 28 and 90 days of curing. Test results confirmed that the addition of zeolite was promising and favourable in enhancing the compressive strength, crack resistance and reducing the autogenous shrinkage of HPC due to synergistic pozzolanic and internal curing effects. The autogenous shrinkage tended to decrease with the increase in zeolite content and its particle size. In addition, the extent of the autogenous shrinkage development at the early ages decreased with higher zeolite content replaced. Furthermore, to predict the autogenous shrinkage of HPC containing zeolite, an improved model has been proposed, in which the conventional ultimate autogenous shrinkage strain and time function were modified by introducing new parameters accounting for the zeolite content and its particle size. It appeared that the proposed model was able to capture the autogenous shrinkage behaviour of HPC with or without zeolite, while the fib 2010 model underestimated the autogenous shrinkage of HPC containing less than 10% zeolite replacement.
This research investigated the effect of fly ash content on the compressive strength development of ultra-high-performance concrete (UHPC) at different curing conditions, i.e., the standard curing condition and the heat curing. A total of 20 mixtures were prepared to cast specimens to measure the compressive strength at different ages from 3 days to 180 days. Additionally, 300 specimens were prepared to estimate the appropriate heat curing period at the early ages in terms of enhancing the 28-day compressive strength of UHPC with high content of fly ash (FA). From the regression analysis using test data, empirical equations were formulated to assess the compressive strength development of UHPC considering the FA content and maturity function. Test results revealed that the preference of the addition of FA for enhancing the compressive strength of UHPC requires the early heat curing procedure which can be recommended as at least 2 days under 90 °C. Moreover, the compressive strength of UHPC with FA under heat curing mostly reached its 28-day strength within 3 days. The proposed models based on the fib 2010 model can be a useful tool to reliably assess the compressive strength development of UHPC with high-volume fly ash (HVFA) (up to 70% fly ash content) under a heat curing condition that possesses a different performance from that of normal- and high-strength concrete. When 50% of the cement content was replaced by FA, the embodied CO2 emission for UHPC mixture reduced up to approximately 50%, which is comparable to the CO2 emission calculated from the conventional normal-strength concrete.
Bài báo này trình bày kết quả nghiên cứu thực nghiệm khả năng chịu tác động tải trọng nổ của bê tông chất lượng siêu cao (Ultra-High Performance Concrete - UHPC). Bê tông UHPC sử dụng trong nghiên cứu được chế tạo sử dụng các vật liệu sẵn có ở Việt Nam. Các tấm bê tông UHPC và bê tông thường có cùng kích thước (chiều dài 1000 mm, chiều rộng 800 mm và chiều dày 120 mm) đã được chế tạo và thí nghiệm nổ để so sánh. Tải trọng nổ sử dụng là thuốc nổ nhũ tương. Sự hư hại và phá hủy ở mặt trên, mặt dưới của các mẫu thí nghiệm và thành phần hạt của các mãnh vỡ bắn ra dưới tác động của tải trọng nổ được phân tích và so sánh giữa bê tông UHPC và bê tông thường.
Từ khóa:
bê tông chất lượng siêu cao; bê tông thường; tải trọng nổ; thực nghiệm.
Bài báo này trình bày về nghiên cứu ảnh hưởng của một số phụ gia khoáng (PGK) đến đặc tính ăn mòn cốt thép trong bê tông chất lượng siêu cao (BTCLSC). Trong nghiên cứu này, PGK sử dụng bao gồm silica fume (SF), tro bay (FA) và xỉ lò cao hạt hóa nghiền mịn (GGBFS) được sử dụng để thay thế xi măng theo tỷ lệ SF sử dụng 10% và 20%; FA sử dụng 10% và 20%; GGBFS sử dụng 20%, 40% theo khối lượng chất kết dính. Kết quả nghiên cứu cho thấy với mẫu BTCLSC sử dụng PGK cho khả năng chống ăn mòn của cốt thép trong bê tông tốt hơn so với mẫu không sử dụng PGK và với mẫu bê tông thường (cường độ nén khoảng 30 MPa). Mức độ ăn mòn cốt thép của mẫu BTCLSC sử dụng GGBFS và SF thấp hơn so với mẫu sử dụng FA.
Nhận ngày 10/01/2018; sửa xong 24/01/2018; chấp nhận đăng 28/02/2018
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.