Al2O3/SiC particulate reinforced metal matrix composites were produced by a stir casting process. The Al2O3/SiC powder mix was prepared by reaction of aqueous solution of aluminium sulphate, ammonium sulphate and water containing SiC particles at 1200• C. 10 wt% of this hybrid ceramic powder with dierent sized SiC particles was added to a liquid matrix alloy during a mechanical stirring between solidus and liquidus under inert conditions. Dry sliding wear tests were conducted with a pin-on-disk friction and wear tester. The morphologies of the worn surfaces were examined using a scanning electron microscope to observe the wear characteristics and investigate the wear mechanism. An optical microscope was used to examine the precipitations of the hybrid ceramic reinforced metal matrix composites after wear tests at room temperature under dry conditions. It was found that hybrid and bimodal particle reinforcement decreased weight loss especially when SiC powder with larger grain size was used. Microstructural examination showed that besides occurring coarse SiC particle reinforcement, a ne alumina particle reinforcement phase was observed within the aluminium matrix (A332). The improvement in wear resistance of the hybrid ceramic reinforced metal matrix composites could be attributed to the ability of the larger SiC particles to carry a greater portion of the applied load, as well as to the function of the larger SiC particles in protecting the smaller alumina particles from being gouged out during the wear process. Furthermore, the incorporation of hybrid and bimodal particles increased hardness of the composites with respect to the composite with fully small sized particles.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.