Hydrogels are being investigated recently for the bioactive molecules (in particular pharmaceutical proteins) controlled release, such as matrices, and for the living cells encapsulation. Biodegradable nature of hydrogels has created much interest for drug delivery systems. The original three-dimensional structure disintegrates into nontoxic substances to ascertain an excellent biocompatibility of the gel. Chemical cross-linking is the highly resourceful method for the formation of hydrogels having an excellent mechanical strength. Cross-linkers used in hydrogel preparation should be extracted from the hydrogels before use due to their reported toxicity. Physically cross-linked methods for preparation of hydrogel are the alternate solution of cross-linker toxicity.
This present work was aimed at synthesizing pH-sensitive cross-linked AA/Gelatin hydrogels by free radical polymerization. Ammonium persulfate and ethylene glycol dimethacrylate (EGDMA) were used as initiator and as cross-linking agent, respectively. Different feed ratios of acrylic acid, gelatin, and EGDMA were used to investigate the effect of monomer, polymer, and degree of cross-linking on swelling and release pattern of the model drug. The swelling behavior of the hydrogel samples was studied in 0.05 M USP phosphate buffer solutions of various pH values pH 1.2, pH 5.5, pH 6.5, and pH 7.5. The prepared samples were evaluated for porosity and sol-gel fraction analysis. Pheniramine maleate used for allergy treatment was loaded as model drug in selected samples. The release study of the drug was investigated in 0.05 M USP phosphate buffer of varying pH values (1.2, 5.5, and 7.5) for 12 hrs. The release data was fitted to various kinetic models to study the release mechanism. Hydrogels were characterized by Fourier transformed infrared (FTIR) spectroscopy which confirmed formation of structure. Surface morphology of unloaded and loaded samples was studied by surface electron microscopy (SEM), which confirmed the distribution of model drug in the gel network.
)} compared to control group. The mean difference in glycemic control between both groups was insignificant but mild reductions were seen in fasting blood glucose p = 0.12). A significant increase in disease-related knowledge was seen in the intervention group, compared to the control group which was evident by mean differences in compliance (p = 0.003), foot-care (p < 0.001) and self-monitoring of blood glucose (p = 0.001
In the present work crosslinked hydrogels based on chitosan (CS) and acrylic acid (AA) were prepared by free radical polymerization with various feed compositions using N,N methylenebisacrylamide (MBA) as crosslinking agent. Benzoyl peroxide was used as catalyst. Fourier transform infrared spectra (FTIR) confirmed the formation of the crosslinked hydrogels. This hydrogel is formed due to electrostatic interaction between cationic groups in CS and anionic groups in AA. Prepared hydrogels were used for dynamic and equilibrium swelling studies. For swelling behavior, effect of pH, polymeric and monomeric compositions and degree of crosslinking were investigated. Swelling studies were performed in USP phosphate buffer solutions of varying pH 1.2, 5.5, 6.5 and 7.5. Results showed that swelling increased by increasing AA contents in structure of hydrogels in solutions of higher pH values. This is due to the presence of more carboxylic groups available for ionization. On the other hand by increasing the chitosan content swelling increased in a solution of acidic pH, but this swelling was not significant and it is due to ionization of amine groups present in the structure of hydrogel. Swelling decreased with increase in crosslinking ratio owing to tighter hydrogel structure. Porosity and sol-gel fraction were also measured. With increase in CS and AA contents porosity and gel fraction increased, whereas by increasing MBA content porosity decreased and gel fraction increased. Furthermore, diffusion coefficient (D) and the network parameters i.e., the average molecular weight between crosslinks (M(c)), polymer volume fraction in swollen state (V(2s)), number of repeating units between crosslinks (M(r)) and crosslinking density (q) were calculated using Flory-Rehner theory. Selected samples were loaded with a model drug verapamil. Release of verapamil depends on the ratios of CS/AA, degree of crosslinking and pH of the medium. The release mechanisms were studied by fitting experimental data to model equations and calculating the corresponding parameters. The result showed that the kinetics of drug release from the hydrogels in both pH 1.2 and 7.5 buffer solutions was mainly non-Fickian diffusion.
The aim of the present study was to extend the use of flurbiprofen in clinical settings by avoiding its harmful gastric effects. For this purpose, we designed the controlled release solid lipid flurbiprofen microspheres (SLFM) by emulsion congealing technique. Drug was entrapped into gastro resistant biodegradable beeswax microspheres which were prepared at different drug/beeswax ratios 1:1, 1:2 and 1:3 using gelatin and tween 20 as emulsifying agents. The effect of emulsifiers and the effect drug/beeswax ratios were studied on hydration rate, encapsulating efficiency, micromeritic properties, scanning electron microscopy (SEM), fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), X-ray diffraction (X-RD) analysis and in vitro drug release at pH 1.2 for 2 h and at pH 6.8 for 10 h. SEM revealed that microspheres made with tween 20 were smooth while microspheres made with gelatin showed porous morphology, however, they were all spherical in nature. The practical yield (recovery) showed a dependence on drug-beeswax ratio and it was variable from 53 to 84%. High loading encapsulating efficiency of flurbiprofen from 8 to 94% was achieved. FTIR and DSC analysis confirmed the absence of any drug polymer interaction indicating drug stability during microencapsulation. X-RD of pure flurbiprofen shows sharp peaks, which decreases on encapsulation, indicating decrease in the crystallinity of drug in microspheres. The micromeritic studies confirmed the presence of excellent and good flow properties of microspheres. Entrapment efficiency, morphology, practical yield, hydration rate, flow properties demonstrated their dependence on the HLB value of emulsifiers and emulsifiers with higher HLB were found more appropriate for effective microencapsulation of flurbiprofen. The release kinetics followed zero order mechanism of drug release at pH 6.8. Release pattern depends on the morphology of flurbiprofen microspheres and amount of beeswax used in the microspheres preparation. The microspheres prepared with high HLB values i.e., tween 20 showed effective control of drug release from microspheres. The absence of drug release at pH 1.2 proved the suitability of beeswax for its use as a gastro resistant material.
In this study, we fabricated pH-sensitive polyvinylpyrrolidone/acrylic acid (PVP/AA) hydrogels by a free-radical polymerisation method with variation in the content of monomer, polymer and cross-linking agent. Swelling was performed in USP phosphate buffer solutions of pH 1.2, 5.5, 6.5 and 7.5 with constant ionic strength. Network structure was evaluated by different parameters and FTIR confirmed the formation of cross-linked hydrogels. X-ray crystallography showed molecular dispersion of tramadol HCl. A drug release study was carried out in phosphate buffer solutions of pH 1.2, 5.5 and 7.5 for selected samples. It was observed that swelling and drug release from hydrogels can be modified by changing composition and degree of cross-linking of the hydrogels under investigation. Swelling coefficient was high at higher pH values except for the one containing high PVP content. Drug release increased by increasing the pH of the medium and AA contents in hydrogels while increasing the concentration of cross-linking agent had the opposite effect. Analysis of the drug release mechanism revealed non-Fickian transport of tramadol from the hydrogels.Uniterms: Drugs/release. Hydrogels/pH sensitive. Polyvinylpyrrolidone-acrilic acid/hidrogels. Tramadol hydrochloride. Methylene bisacrylamide.Nesse estudo, preparamos hidrogéis de polivinilpirrolidona/ácido acrílico(PVP/AA), sensíveis ao pH, por meio de método de polimerização de radical livre, com variações no conteúdo de monômero, de polímero e de agente de ligação cruzada. O inchamento foi realizado em soluções tampão fosfato USP pH 1,2, 5,5, 6,5 e 7,5, com força iônica constante. A estrutura reticular foi avaliada por diferentes parâmetros e o FTIR confirmou a formação de hidrogéis de ligação cruzada. A cristalografia de raios X mostrou dispersão molecular do cloridrato de tramadol. Realizou-se estudo de liberação do fármaco em soluções tampão fosfato pH 1,2, 5,5 e 7,5 para amostras selecionadas. Observou-se que o inchamento e a liberação do fármaco dos hidrogéis podem ser modificados mudando-se a composição e o grau de ligação cruzada dos hidrogéis em estudo. O coeficiente de inchamento foi alto em pH mais altos, exceto para um deles com alto conteúdo de PVP. A liberação do fármaco aumentou com o aumento do pH do meio e do conteúdo em AA nos hidrogéis, enquanto que o aumento na concentração do agente de ligação cruzada apresentou efeito oposto. A análise do mecanismo de liberação do fármaco revelou transporte não Fickiano do tramadol dos hidrogéis.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
334 Leonard St
Brooklyn, NY 11211
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.